Cracking mechanism in a laser powder bed fused cold-work tool steel: The role of residual stresses, microstructure and local elemental concentrations
نویسندگان
چکیده
Laser powder bed fusion (LPBF) facilitates economic advantages by enhancing cutting speeds of tools through the implementation complex internal cooling channels that could not be fabricated otherwise. However, tool steels are prone to cracking during cyclic remelting process with extremely fast rates due their high carbon and alloying element contents related stresses. In this work, a correlation between microscopic crack patterns in steel processed via LPBF, residual stress gradients, local microstructure near-crack elemental concentrations is studied using longitudinal/transverse sectional synchrotron X-ray micro-diffraction, electron microscopy techniques atom probe tomography. A formation horizontal micro-cracks correlates drops, especially at geometrically notched positions sample edges. Remarkably, cracks propagate predominantly along network eutectic intergranular carbides type M2C deposited grain boundaries martensite retained austenite matrix. comparison representative carbide sizes surfaces within crack-free regions indicates preferably transcrystalline manner, whereas no observed. The observations link propagation solidification prevailing network. Therefore, stress-induced carbides, which formed fracture solid state tensile accumulations, was found as predominant mechanism LPBF process.
منابع مشابه
Study of the Microstructure and Cracking Mechanisms of Hastelloy X Produced by Laser Powder Bed Fusion
Hastelloy X (HX) is a Ni-based superalloy which suffers from high crack susceptibility during the laser powder bed fusion (LPBF) process. In this work, the microstructure of as-built HX samples was rigorously investigated to understand the main mechanisms leading to crack formation. The microstructural features of as-built HX samples consisted of very fine dendrite architectures with dimensions...
متن کاملThe Effect of Deep Cryogenic Treatment on Microstructure, Hardness and Wear Behavior of INDRA 5 Cold Work Tool Steel
متن کامل
Hydrogen Assisted Cracking in Pearlitic Steel Rods: The Role of Residual Stresses Generated by Fatigue Precracking
Stress corrosion cracking (SCC) of metals is an issue of major concern in engineering since this phenomenon causes many catastrophic failures of structural components in aggressive environments. SCC is even more harmful under cathodic conditions promoting the phenomenon known as hydrogen assisted cracking (HAC), hydrogen assisted fracture (HAF) or hydrogen embrittlement (HE). A common way to as...
متن کاملthe analysis of the role of the speech acts theory in translating and dubbing hollywood films
از محوری ترین اثراتی که یک فیلم سینمایی ایجاد می کند دیالوگ هایی است که هنرپیش گان فیلم میگویند. به زعم یک فیلم ساز, یک شیوه متأثر نمودن مخاطب از اثر منظوره نیروی گفتارهای گوینده, مثل نیروی عاطفی, ترس آور, غم انگیز, هیجان انگیز و غیره, است. این مطالعه به بررسی این مسأله مبادرت کرده است که آیا نیروی فراگفتاری هنرپیش گان به مثابه ی اعمال گفتاری در پنج فیلم هالیوودی در نسخه های دوبله شده باز تولید...
15 صفحه اولthe role of russia in transmission of energy from central asia and caucuses to european union
پس ازفروپاشی شوروی،رشد منابع نفت و گاز، آسیای میانه و قفقاز را در یک بازی ژئوپلتیکی انرژی قرار داده است. با در نظر گرفتن این منابع هیدروکربنی، این منطقه به یک میدانجنگ و رقابت تجاری برای بازی های ژئوپلتیکی قدرت های بزرگ جهانی تبدیل شده است. روسیه منطقه را به عنوان حیات خلوت خود تلقی نموده و علاقمند به حفظ حضورش می باشد تا همانند گذشته گاز طبیعی را به وسیله خط لوله مرکزی دریافت و به عنوان یک واس...
15 صفحه اولذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Acta Materialia
سال: 2022
ISSN: ['1873-2453', '1359-6454']
DOI: https://doi.org/10.1016/j.actamat.2021.117570