Crack Property Dur to Thermal Stress for ZrO2-NiCrAlY Plasma Sprayed Layer.

Microstructure and Properties of Plasma Sprayed Nanostructural ZrO2 Coatings

Plasma sprayed zirconia deposits have been employed in wide applications for thermal protection. Recently, the use of nanostructural surface represents an alternative for improving the performance of these coatings. The present paper reviewed the works in this field at our research group, including synthesis of nanostructural ZrO2 powders, influence of spraying parameters on microstructure and ...

Air Plasma Sprayed Bond Coat Oxidation Behavior and its Resistance to Isothermal and Thermal Shock Loading

An experimental investigation was conducted to find the effect of spraying method of coating of Thermal Barrier Coatings (TBCs) on their oxidation behaviour and resistance to various thermal loading. Isothermal and thermal shock tests were performed in order to study oxidation behaviour of air plasma sprayed Bond Coat (BC) and assess its effect on TBCs lifetime under the stated loadings. Specim...

High-temperature degradation of plasma sprayed thermal barrier coating systems

Thermal barrier coating systems (TBCs) are used in gas turbines to prevent high-temperature degradation of metallic materials in the combustor and turbine. One of the main concerns regarding TBCs is poor reliability, and accurate life prediction models are necessary in order to fully utilise the beneficial effects of TBCs. This research project aims at developing deeper understanding of the deg...

AN INVESTIGATION ON EFFECT OF BOND COAT REPLACEMENT ON HOT CORROSION PROPERTIES OF THERMAL BARRIER COATINGS

In the present study NiCrAlY bond coating layer was produced by electroplating against common atmospheric plasma spraying (APS). Both types of the bond coats were applied on IN738LC base metal then, the YSZ (ZrO2-8% Y2O3) thermal barrier top layer was coated by atmospheric plasma spray technique. Hot corrosion is one of the main destructive factors in thermal barrier coatings (TBCs) which come ...

Failure analysis of suspension plasma sprayed thermal barrier coatings