Crack growth behavior of low-alloy bainitic 51CrV4 steel
نویسندگان
چکیده
منابع مشابه
Crack Behavior of the Aluminum Alloy 2024 Under Fretting Conditions
The initial stage of fretting fatigue crack growth is significantly influenced by tangential force induced by fretting action along the contact surface where a mixed-mode crack growth is involved. Fretting crack behavior of aluminum alloy 2024 was studied, taking into account the problem of contact asperities. Finite element was used for the determination of the stress field near the contact su...
متن کاملThe Evaluation of Corrosion Behavior of AISI 347 Stainless Steel to ASTM A335 Low Alloy Steel Dissimilar Welds
In the present study, the corrosion behavior of AISI 347 austenitic stainless steel to ASTM A335 low alloy steel dissimilar joint was investigated. For this purpose, two filler metals, ER309L and ERNiCr-3, were selected to be used during the gas tungsten arc welding process. To investigate the corrosion behavior of the joints after welding, the specimens were tested in 3.5% sodium chloride solu...
متن کاملCorrosion behavior of dissimilar welded joint between Inconel 617 alloy and A387-Gr.11 low-alloy steel
In this study, Inconel 617 alloy was welded to A387-Gr.11 low-alloy steel using ER309L filler metal via gas tungsten arc welding (GTAW). First, the corrosion behavior of Inconel 617, A387-Gr, and the weld metal was evaluated by the Tafel polarization test and electrochemical impedance spectroscopy (EIS) in acidic (H2SO4), neutral (NaCl), and combined (H2SO4 + NaCl) solution at ambient temperatu...
متن کاملThe Ballistic Behavior of High Strength, Low Alloy-100 Steel at Sub-zero Temperatures
The ballistic response of the high strength, low alloy (HSLA-100) steel at ambient and temperatures of -400°C, -800°C and -1960°C is investigated in this work. Lambert-jonas equation is used to fit the experimental results into a curve. The effect of quenching on ballistic behavior of HSLA-100 is also studied. The experiments are conducted on 3mm thick rectangular specimens impacted by blunt ti...
متن کاملCorrosion behavior of dissimilar welded joint between Inconel 617 alloy and A387-Gr.11 low-alloy steel
In this study, Inconel 617 alloy was welded to A387-Gr.11 low-alloy steel using ER309L filler metal via gas tungsten arc welding (GTAW). First, the corrosion behavior of Inconel 617, A387-Gr, and the weld metal was evaluated by the Tafel polarization test and electrochemical impedance spectroscopy (EIS) in acidic (H2SO4), neutral (NaCl), and combined (H2SO4 + NaCl) solution at ambient temperatu...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Procedia Engineering
سال: 2010
ISSN: 1877-7058
DOI: 10.1016/j.proeng.2010.03.149