Crack-Growth Behavior in Thermal Barrier Coatings with Cyclic Thermal Exposure
نویسندگان
چکیده
منابع مشابه
Influence of Cyclic Thermal Loading on Fatigue Behavior of Thermal Barrier Coatings
Thermally insulating ceramic coatings also known as thermal barrier coatings (TBCs) have been essential technologies to improve the performance and efficiency of advanced gas turbines in service at extremely high temperatures. The damage mechanisms of air-plasma sprayed YSZ thermal barrier coatings (TBC) with various microstructures were studied by microscopic techniques after thermal cycling. ...
متن کاملThermal Fatigue Behavior of Air-Plasma Sprayed Thermal Barrier Coating with Bond Coat Species in Cyclic Thermal Exposure
The effects of the bond coat species on the delamination or fracture behavior in thermal barrier coatings (TBCs) was investigated using the yclic thermal fatigue and thermal-shock tests. The interface microstructures of each TBC showed a good condition without cracking or delamination after flame thermal fatigue (FTF) for 1429 cycles. The TBC with the bond coat prepared by the air-plasma spray ...
متن کاملCrack propagation in thermal barrier coating systems
Thermal barrier coating systems are used on top of highly stressed components in gas turbines to protect the nickel-based substrates. A well-established thermal barrier coating system consist of the bond-coat (BC) and the thermal barrier coating (TBC). A third layer is grown during service: the thermally grown oxide (TGO) between the BC and the TBC. The coatings fail in service because of diffe...
متن کاملThermal Barrier Ceramic Coatings — A Review
Thermal barrier coatings (TBCs) provide effective thermal barrier to the components of gas turbine engines by allowing higher operating temperatures and reduced cool‐ ing requirements. Plasma spraying, electron-beam physical vapor deposition, and sol‐ ution precursor plasma spray techniques are generally used to apply the TBCs on the metallic substrates. The present article addresses the TBCs f...
متن کاملMicrostructural investigations of EBPVD thermal barrier coatings
This paper deals with the morphology, constitutive phases and fine microstructures of some EBPVD processed yttria partially stabilized zirconia thermal barrier coatings. This study has been performed by X-ray diffraction and scanning and transmission electron microscopy. It was shown that the coatings studied were constituted of a single metastable tetragonal t' phase, as expected if one refers...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Coatings
سال: 2019
ISSN: 2079-6412
DOI: 10.3390/coatings9060365