Cover cracking model in reinforced concrete structures subject to rebar corrosion
نویسندگان
چکیده
منابع مشابه
Experimental Investigation of Corrosion Cracking in Reinforced Concrete Beams Containing Nano Wollastonite
Cracking of the concrete cover due to corrosion is defined as the serviceability limit state of reinforced concrete structures. This study evaluated the influence of a mineral admixture i.e. nano wollastonite on corrosion performance and serviceability of reinforced concrete structures by performing an accelerated corrosion test on ten reinforced concrete beams under a sustained load. To do so,...
متن کاملCorrosion-Induced Concrete Cracking Model Considering Corrosion-Filled Paste
A TCP–TCL model is established to describe the relationship between the thickness of the corrosion-filled paste (CP) and that of the corrosion layer (CL). This model can describe the phenomenon that the corrosion filling in the concrete pores and accumulating at the steel/concrete interface occur synchronously. Based on the TCP–TCL model, a corrosion-induced concrete cracking model, which can q...
متن کاملBoric Acid Corrosion of Concrete Rebar
Borated water leakage through spent fuel pools (SFPs) at pressurized water reactors is a concern because it could cause corrosion of reinforcement steel in the concrete structure and compromise the integrity of the structure. Because corrosion rate of carbon steel in concrete in the presence of boric acid is lacking in published literature and available data are equivocal on the effect of boric...
متن کاملMonitoring Corrosion of Steel Bars in Reinforced Concrete Structures
Corrosion of steel bars embedded in reinforced concrete (RC) structures reduces the service life and durability of structures causing early failure of structure, which costs significantly for inspection and maintenance of deteriorating structures. Hence, monitoring of reinforcement corrosion is of significant importance for preventing premature failure of structures. This paper attempts to pres...
متن کاملCORROSION BEHAVIOR OF ZINC COATED STEEL REBAR IN HIGH-STRENGTH REINFORCED CONCRETE
A large number of reinforced concrete structures subjected to chloride ions. Two basicapproaches for preventing corrosion of reinforcing steel embedded in concrete are: Increasing theconsolidation of concrete and using different coating on rebars. In present research steel rebarsare coated in different ways: a) 40 µm of zinc electroplated on steel rebar b) Zinc powder withepoxy paste (zinc rich...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Zhejiang University SCIENCE A
سال: 2014
ISSN: 1673-565X,1862-1775
DOI: 10.1631/jzus.a1300393