CORROSION RESISTANCE OF DYNAMIC LOADED CAST ALLOY AS12
نویسندگان
چکیده
منابع مشابه
Enhancing Wear Resistance of Squeeze Cast AC2A Aluminum Alloy
The effect of squeeze casting process parameters on wear behavior of AC2A aluminium alloy was primarily investigated in this experimental study. Five process parameters, namely squeeze pressure, pouring temperature, die temperature, die material and compression time, each at four levels were chosen and sixteen experimental runs based on L16 orthogonal array were performed. From analysis of vari...
متن کاملDynamic Recrystallization Behavior and Corrosion Resistance of a Dual-Phase Mg-Li Alloy
The hot deformation and dynamic recrystallization behavior of the dual-phase Mg-9Li-3Al-2Sr-2Y alloy had been investigated using a compression test. The typical dual-phase structure was observed, and average of grain size of as-homogenized alloy is about 110 µm. It mainly contains β-Li, α-Mg, Al₄Sr and Al₂Y phases. The dynamic recrystallization (DRX) kinetic was established based on an Avrami t...
متن کاملCorrosion Resistance Tests of Magnesium Alloy We43 after Extrusion
J. Przondziono, E. Hadasik, J.Szala, J. Wieczorek, Faculty of Materials Science and Metallurgy, The Silesian University of Technology, Katowice, Poland, W. Walke, Faculty of Biomedical Engineering, The Silesian University of Technology, Gliwice, Poland The purpose of the study was t o evaluate resistance to electrochemical corrosion of magnesium alloy WE43 after plastic working. Potentiodynamic...
متن کاملINFLUENCE OF LASER SURFACE HARDENING ON CORROSION PROPERTIES OF Al-Zn-Si CAST ALLOY
E. Tillová, L. Kuchariková, M. Chalupová, J. Belan, A. Vaško, I. Švecová, University of Žilina, Faculty of Mechanical Engineering, Slovak Republic This work is focused on the effect of the laser surface treatment (laser power 50 and 80 W) on microstructure and corrosion properties of self-hardened AlZn10Si8Mg cast alloy used for engine and vehicle constructions. The electrochemical impedance sp...
متن کاملEffect of Ti on the Mechanical Properties and Corrosion of Cast AZ91 Magnesium Alloy
Ti addition to AZ91 alloy was been investigated with conventional casting. The microstructure and mechanical property were examined. The Corrosion resistance of all the different Ti addition content alloy was studied in 3.5% NaCl solution through weight loss measurement in constant immersion conditions and potentiodynamic polarization experiments. The results show that addition of Ti with an am...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Litiyo i Metallurgiya (FOUNDRY PRODUCTION AND METALLURGY)
سال: 2017
ISSN: 2414-0406,1683-6065
DOI: 10.21122/1683-6065-2017-2-70-75