Corrosion resistance of alumina-magnesia castable to slag in steel ladle lining
نویسندگان
چکیده
منابع مشابه
The Effect of Carbon Nanoparticles and Calcined Alumina on Mechanical Properties and Corrosion Resistance Behavior of the Magnesia Carbon Refractories
Nowadays, magnesia carbon refractories are very important for the iron and steel industries. It is due to their unique properties, such as low wet ability with melt iron and steel. Therefore, it is important to extend the life of the refractory. In this research, the effect of calcined alumina and nano carbon on mechanical strength and corrosion resistance against slag in magnesia carbon refrac...
متن کاملDifferent Damaged Shaft Lining Concrete Resistance to Sulfate Corrosion
Shaft lining concrete itself has a certain degree of initial damage before being corroded by sulfate. In order to study the resistance of the concrete of the initial damage in different corrosion solution concentration of sulfate, samples of concrete without initial damage, loaded 50% ultimate load and loaded 70% ultimate load with initial damage concrete were selected and studied their corrosi...
متن کاملHot Corrosion of Slag Line in Plaster of Tundish in Continuous Casting of Steel
Plasters are produced from a light refractory material, mainly MgO (M.P. 2800ºC), a binder, and a void forming substance for insulating purposes. Different oxides from the slag penetrate into these voi...
متن کاملAlumina nanostructured coating for corrosion protection of 316L stainless steel
Nanostructured alumina thin films were coated on stainless steel by Sol-Gel dip coating method. In order to prevent crack formation, Al2O3 films were kept in a solvent bath immediately after coating to reduce the rate of drying. Effects of calcination temperature and withdrawal speed on structural properties were analyzed using XRD and SEM. Topography and thickness of coat...
متن کاملAlumina nanostructured coating for corrosion protection of 316L stainless steel
Nanostructured alumina thin films were coated on stainless steel by Sol-Gel dip coating method. In order to prevent crack formation, Al2O3 films were kept in a solvent bath immediately after coating to reduce the rate of drying. Effects of calcination temperature and withdrawal speed on structural properties were analyzed using XRD and SEM. Topography and thickness of coat...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Ceramic Society of Japan
سال: 2011
ISSN: 1882-0743,1348-6535
DOI: 10.2109/jcersj2.119.916