Alumina nanostructured coating for corrosion protection of 316L stainless steel
Nanostructured alumina thin films were coated on stainless steel by Sol-Gel dip coating method. In order to prevent crack formation, Al2O3 films were kept in a solvent bath immediately after coating to reduce the rate of drying. Effects of calcination temperature and withdrawal speed on structural properties were analyzed using XRD and SEM. Topography and thickness of coat...
متن کاملAlumina nanostructured coating for corrosion protection of 316L stainless steel
Nanostructured alumina thin films were coated on stainless steel by Sol-Gel dip coating method. In order to prevent crack formation, Al2O3 films were kept in a solvent bath immediately after coating to reduce the rate of drying. Effects of calcination temperature and withdrawal speed on structural properties were analyzed using XRD and SEM. Topography and thickness of coat...
متن کاملHydrophobic and superhydrophobic coatings for corrosion protection of steel
Since metals in general, and steels in particular, are vital construction materials in our modern society, the corrosion protection of said materials is of great importance, both to ensure safety and to reduce costs associated to corrosion. Previously, chromium (VI) and other harmful substances were effectively used to provide corrosion protection to steel, but since their use was heavily regul...
متن کاملCorrosion Protection of Steel Using Nonanomalous Ni-Zn-P Coatings
A novel technique for obtaining nonanomalous Ni-Zn-P coatings with high Ni content ~74 wt % as compared to 15-20 wt % in the conventional plating method! has been developed. These coatings show promise as a replacement for Cd in sacrificially protecting steel. Ni-Zn-P coatings were deposited using an electroless method from a solution containing NiSO4 , complexing agent and ammonium chloride. V...
متن کاملNew Developments in Steel Reinforcement Protection From Corrosion
Due to life-cycle costs considerations, the Federal Highway Administration has required that all their new bridge structures have a service life of more than 75 years. The practical use of adequate concrete cover, low water/cement ratio, and corrosion inhibitors and admixtures are not enough to satisfy this requirement. Corrosion still affects the reinforcing steel through the diffusion of chlo...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: CORROSION ENGINEERING
سال: 1989
ISSN: 0010-9355,1884-1155
DOI: 10.3323/jcorr1974.38.10_546