Corrosion Products and Corrosion Rates of Cast Iron in Flowing Sea and Fresh Water at High Temperature
نویسندگان
چکیده
منابع مشابه
Corrosion Properties of F82H in Flowing High Temperature Pressurized Water
This work reports the effects of water flow and dissolved oxygen (DO) on corrosion behavior of reduced activation ferritic/martensitic steel, F82H. The corrosion tests were performed in high temperature pressurized water by using a test apparatus for rotated disk sample. All of specimens showed weight gains after static corrosion tests up to 500 h. However, the rotated disk showed weight losses...
متن کاملNitrogen and Water in High Temperature Corrosion
Service life-time of alloys used in high temperature applications is often limited by corrosion. FeCrAl(Re) alloys are partially designed to form a protective α-alumina oxide scale at elevated temperatures in order to mitigate further oxidation. The scale growth commonly follows a parabolic rate law, which under a Wagnerian setting depends on transport of charged species; ions, vacancies and el...
متن کاملHigh-temperature Corrosion Behavior of Iron Aluminide Alloys and Coatings
A multi-year effort has been focused on optimizing the long-term oxidation performance of ingot-processed (IP) and oxide-dispersion strengthened (ODS) Fe3Al and iron aluminidebased coatings. Based on results from several composition iterations, a Hf-doped alloy (Fe28Al-2Cr-0.05at.%Hf) has been developed with significantly better high temperature oxidation resistance than other iron aluminides. ...
متن کاملTemperature Effects on Iron Corrosion
Temperature is an often overlooked water quality parameter that may influence corrosion of iron pipes in drinking water distribution systems. This study examined corrosion of cast iron samples in an aerobic, microbially stable water at different constant temperatures (5, 20, and 25°C) as well as in waters where the temperature continuously cycled (17.5 – 23°C and 5 – 20°C). The composition and ...
متن کاملCorrosion of Concrete in Sea Water (RESEARCH NOTE)
Attack and disintegration of concrete structures under the influence of aggressive fluids, wet gases, etc. are understood as corrosion of concrete. The corrosion of concrete is a chemical, colloidchemical process, yet often a physico-chemical one, while that of reinforced concrete supported oil platforms are subjected to marine environment in the Persian Gulf and therefore corroded. In the pres...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: CORROSION ENGINEERING
سال: 1989
ISSN: 0010-9355,1884-1155
DOI: 10.3323/jcorr1974.38.5_255