Corrosion of chromium containing alloys in non-steady state environments containing oxygen, carbon, and chlorine
نویسندگان
چکیده
منابع مشابه
Corrosion of chromium containing alloys in non-steady state environments containing oxygen, carbon, and chlorine
Internal attack of chromium containing alloys in mixed oxygen-chlorine environments occurs by the formation of pores which penetrate down grain boundaries of the alloys. No internal attack was detected in a binary Fe-20 %Cr alloy at 1200 K in environments containing 2500 ppm C12. The rate of internal attack of alloy 800H in such environments was increased by replacing the O2 in the gas by C02 ....
متن کاملCorrosion mechanism of Ti-Cr alloys in solution containing fluoride.
OBJECTIVE The objective of this study was to clarify the influence of chromium content on surface reaction of Ti-Cr alloys in an acidic fluoride-containing saline solution. METHODS Four Ti-Cr alloys containing 5, 10, 15 or 20 mass% chromium were characterized in terms of dissolution of metals in an acidic fluoride-containing saline solution and surface structure by X-ray photoelectron spectro...
متن کاملOxygen Adsorption on Nitrogen Containing Carbon Surfaces
Introduction The reaction of O2 with carbonaceous surfaces has been widely studied due to its important application in industry. In general, O2 is first chemisorbed on an electron-rich site of the carbon basal plane of graphite and then, it dissociates into oxygen atoms. Oxygen will diffuse on the surface until finds a structural defect to form covalent bonds. If temperature is appropriated, CO...
متن کاملPractical Corrosion Control Measures for Elemental Sulfur Containing Environments
This paper provides an overview of materials’ performance in well environments containing H2S and elemental sulphur (S). Based on this information the factors affecting the service life of materials used for well completion and surface facilities in highly sour environments are discussed and limitations on materials selection and chemical inhibition procedures are suggested.
متن کاملMulti-functional magnesium alloys containing interstitial oxygen atoms
A new class of magnesium alloys has been developed by dissolving large amounts of oxygen atoms into a magnesium lattice (Mg-O alloys). The oxygen atoms are supplied by decomposing titanium dioxide nanoparticles in a magnesium melt at 720 °C; the titanium is then completely separated out from the magnesium melt after solidification. The dissolved oxygen atoms are located at the octahedral sites ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Le Journal de Physique IV
سال: 1993
ISSN: 1155-4339
DOI: 10.1051/jp4:1993912