Corrosion fatigue behavior of extruded AZ80, AZ61, and AM60 magnesium alloys in distilled water
نویسندگان
چکیده
منابع مشابه
Fatigue behaviour and fractography of extruded AZ80 magnesium alloys in very high cycle regime
In order to investigate the fatigue properties of extruded magnesium alloy in very high-cycle regime, rotary bending fatigue test was performed in ambient atmosphere at room temperature using the hourglass shaped specimens of AZ80 alloys extruded (Fspecimen) and treated by an artificial aging after extrusion (T5-specimen). From the experimental results, both specimens show a clear step-wise S-N...
متن کاملThe Effect of Environmental Parameters on the Corrosion Behavior of Simple Shear Extruded AZ91 Magnesium Alloys
In this study, the effects of forming method (extrusion) and environmental factors (solution pH and temperature) on the corrosion performance of AZ91 magnesium alloys were investigated using potentiodynamic polarization, electrochemical impedance spectroscopy (EIS), scanning electron microscopy (SEM) and salt spray techniques. The polarization test results of the specimens showed that simple sh...
متن کاملNotch Effects in Tensile Behavior of AM60 Magnesium Alloys
The deformation and failure behavior of an AM60 magnesium alloy was investigated using tensile test on circumferentially notched specimens with different notch radii. The strain and stress triaxiality corresponding to the failure point were evaluated using both analytical and finite element analyses. Combining with systematical observations of the fracture surfaces, it is concluded that deforma...
متن کاملthe effect of environmental parameters on the corrosion behavior of simple shear extruded az91 magnesium alloys
in this study, the effects of forming method (extrusion) and environmental factors (solution ph and temperature) on the corrosion performance of az91 magnesium alloys were investigated using potentiodynamic polarization, electrochemical impedance spectroscopy (eis), scanning electron microscopy (sem) and salt spray techniques. the polarization test results of the specimens showed that simple sh...
متن کاملCorrelation between the surface chemistry and the atmospheric corrosion of AZ31, AZ80 and AZ91D magnesium alloys
* Corresponding author. Tel: 34 1 3944348; Fax: 34 1 3944357 E-mail: [email protected] ABSTRACT X-ray photoelectron spectroscopy (XPS) was used in order to investigate the correlation between the surface chemistry and the atmospheric corrosion of AZ31, AZ80 and AZ91D magnesium alloys exposed to 98% relative humidity at 50oC. Commercially pure magnesium, used as the reference material, reveale...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Strength of Materials
سال: 2008
ISSN: 0039-2316,1573-9325
DOI: 10.1007/s11223-008-0034-8