Corrosion behaviour of stainless steel reinforcement in concrete
نویسندگان
چکیده
منابع مشابه
Influence of Laser Ablation on Stainless Steel Corrosion Behaviour
Laser ablation is the method for material removing from a surface using pulsed lasers. It is used for surface structuring, laser drilling or laser marking. A change of the corrosion behavior of a base material caused by thermal effects during laser processing is an important problem of this technology. Possibilities of surface modification of stainless steel using laser ablation are presented i...
متن کاملCorrosion at Sulphide Inclusions in Stainless Steel
Auger analysis was performed using a high resolution scanning auger electron microscope and auger electron spectroscopy. Elemental auger contour maps for corroded sulphide inclusions in stainless steel were presented. It was found that the copper enriched-manganese sulphide inclusions were uniformly corroded, which might be due to CU2S deposition on the surface of corroding inclusions. In contr...
متن کاملCorrosion Behavior of Stainless Steel Clad Rebar
Stainless steel clad rebar (SCR) was investigated because it may become a cost-effective means of controlling corrosion in concrete under very aggressive environments. Sound SCR (316L cladding) resisted corrosion in saturated Ca(OH)2 solution (SCS) with up to 5 wt% chloride. Cladding breaks on SCR induced significant corrosion of exposed underlying CS in SCS with only 1 wt% chloride. A computer...
متن کاملElectrode Potential Evaluation of Effect of Inhibitors on the Electrochemical Corrosion Behaviour of Mild Steel Reinforcement in Concrete in H2SO4
The electrochemical corrosion behaviour of mild steel embedded in concrete, and partially immersed in 0.2M H2SO4, was studied in this investigation at ambient temperature by potential monitoring technique. The experimental work was performed with a digital multimeter and a Cu/CuSO4 electrode (CSE) as the reference electrode. Extracts of carica papaya leaves and sodium nitrite (NaNO2) in differe...
متن کاملPitting Corrosion Behaviour of New Corrosion-Resistant Reinforcement Bars in Chloride-Containing Concrete Pore Solution
In this study, the pitting behaviour of a new corrosion-resistant alloy steel (CR) is compared to that of low-carbon steel (LC) in a simulated concrete pore solution with a chloride concentration of 5 mol/L. The electrochemical behaviour of the bars was characterised using linear polarisation resistance (LPR) and electrochemical impedance spectroscopy (EIS). The pitting profiles were detected b...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Corrosion Reviews
سال: 2018
ISSN: 2191-0316,0334-6005
DOI: 10.1515/corrrev-2017-0088