Corrosion Behaviour of Inconel 617 Coated with Silicon Oxides in Impure Helium
نویسندگان
چکیده
منابع مشابه
Corrosion behavior of dissimilar welded joint between Inconel 617 alloy and A387-Gr.11 low-alloy steel
In this study, Inconel 617 alloy was welded to A387-Gr.11 low-alloy steel using ER309L filler metal via gas tungsten arc welding (GTAW). First, the corrosion behavior of Inconel 617, A387-Gr, and the weld metal was evaluated by the Tafel polarization test and electrochemical impedance spectroscopy (EIS) in acidic (H2SO4), neutral (NaCl), and combined (H2SO4 + NaCl) solution at ambient temperatu...
متن کاملCorrosion behavior of dissimilar welded joint between Inconel 617 alloy and A387-Gr.11 low-alloy steel
In this study, Inconel 617 alloy was welded to A387-Gr.11 low-alloy steel using ER309L filler metal via gas tungsten arc welding (GTAW). First, the corrosion behavior of Inconel 617, A387-Gr, and the weld metal was evaluated by the Tafel polarization test and electrochemical impedance spectroscopy (EIS) in acidic (H2SO4), neutral (NaCl), and combined (H2SO4 + NaCl) solution at ambient temperatu...
متن کاملCorrosion Behaviour of Nickel Coated AISI 316 Stainless Steel as a Function of Annealing Temperature
AISI 316 stainless steels were coated with 250 nm Ni film by electron beam deposition and post-annealed at different temperatures with a nitrogen flow of 600 cm3min-1 nitrogen. The prepared samples were corrosion tested in 1.0 M sulphuric acid solution using potentiodynamic technique. Crystallographic and morphological structure of the samples were analyzedanalysed by X-ray diffraction (XRD) an...
متن کاملCorrosion resistance and cytocompatibility of biodegradable surgical magnesium alloy coated with hydrogenated amorphous silicon.
The fast degradation rates in the physiological environment constitute the main limitation for the applications of surgical magnesium alloys as biodegradable hard-tissue implants. In this work, a stable and dense hydrogenated amorphous silicon coating (a-Si:H) with desirable bioactivity is deposited on AZ91 magnesium alloy using magnetron sputtering deposition. Raman spectroscopy and Fourier tr...
متن کاملA Review of the Fatigue Behaviour of Components Coated with Thin Hard Corrosion-Resistant Coatings
This paper provides a review of the state of the art on the study of the fatigue behaviour of mechanical components coated with thin hard corrosion-resistant coatings such as the physically or chemically vapour deposited ones. Some references address the experimental characterization of the fatigue resistance of coated steel and light alloys. Some coatings have been observed to prove effective ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Tetsu-to-Hagane
سال: 1985
ISSN: 0021-1575,1883-2954
DOI: 10.2355/tetsutohagane1955.71.10_1375