Corrosion behaviour of as-cast ZK40 with CaO and Y additions
نویسندگان
چکیده
منابع مشابه
Corrosion Behaviour of Nickel Coated AISI 316 Stainless Steel as a Function of Annealing Temperature
AISI 316 stainless steels were coated with 250 nm Ni film by electron beam deposition and post-annealed at different temperatures with a nitrogen flow of 600 cm3min-1 nitrogen. The prepared samples were corrosion tested in 1.0 M sulphuric acid solution using potentiodynamic technique. Crystallographic and morphological structure of the samples were analyzedanalysed by X-ray diffraction (XRD) an...
متن کاملCooling rate optimization of as-cast consciously cast steel
Abstract: A combination of a finite element method (FEM) algorithm with ANSYS codes and post image processing of NDT ultrasonic images along with laboratory cooling experiments and microstructural analysis provide a guideline to determine the optimum cooling rate for any grade of steel in which the highest productivity can be achieved without any degradation of the cast steel products. The sugg...
متن کاملa comparison of teachers and supervisors, with respect to teacher efficacy and reflection
supervisors play an undeniable role in training teachers, before starting their professional experience by preparing them, at the initial years of their teaching by checking their work within the proper framework, and later on during their teaching by assessing their progress. but surprisingly, exploring their attributes, professional demands, and qualifications has remained a neglected theme i...
15 صفحه اولMicro- and Nano-scale Tribo-Corrosion of Cast CoCrMo
Previous studies have established that some of the wear damage seen on cast CoCrMo joint surface is caused by entrained third-body hard particles. In this study, wet-cell micro-indentation and nano-scratch tests have been carried out with the direct aim of simulating wear damage induced by single abrasive particles entrained between the surfaces of cast CoCrMo hip implants. In situ electrochemi...
متن کاملCorrosion Behaviour of Cardiovascular Stents
Cyclic Potentiodynamic polarization studies were conducted to compare the corrosion resistance of Nitinol cardiovascular stents and stainless steel stents. The tests is to simulate the corrosion behavior of the stents under body condition using Phosphate Buffered Saline (PBS) solution at 37C and following the ASTM F2129-01, Item 2, WK1749, Standard. The results of this study indicate that both ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Transactions of Nonferrous Metals Society of China
سال: 2018
ISSN: 1003-6326
DOI: 10.1016/s1003-6326(18)64676-x