Corrosion Behaviour of Aluminium Engine Block in 3.5% NaCl Solution
نویسندگان
چکیده
منابع مشابه
CORROSION BEHAVIOUR OF A 2219 ALUMINIUM ALLOY TREATED WITH A CHROMATE CONVERSION COATING EXPOSED TO A 3.5 % NaCl SOLUTION
This study investigates the formation of a chromate conversion coating at Al-Cu-Fe-Mn intermetallic sites of an Al2219 alloy and the corrosion initiation at these sites in a 3.5 % NaCl solution, using SEM, AES and EDX. Changes in the surface chemistry were monitored after progressive exposures to the solution up to 42 hours. The coating was found to be thinner and more defective on the intermet...
متن کاملLOCALIZED CORROSION OF A 2219 ALUMINIUM ALLOY EXPOSED TO A 3.5% NaCl SOLUTION
This work is focused on the role of intermetallics in pitting corrosion of Al2219 alloy. Second phase particles were characterized by AES, SAM and EDX. Their behaviour in a solution of NaCl was investigated as a function of exposure time. The results confirmed the cathodic nature of the intermetallics with respect to the aluminium matrix. Corrosion products rich in aluminium and oxygen were fou...
متن کاملElectrochemical assessment of imidazole derivatives as corrosion inhibitors for mild steel in 3.5 NaCl solution
The corrosion inhibition efficiency of benzimidazole, 2-methylbenzimidazole and 2- aminobenzimidazole for mild steel immersed in 3.5 NaCl solution was investigated by electrochemical impedance spectroscopy EIS at concentration range from 10-5 to 10-2 M of imidazoles and temperature range from 30 to 50°C. In addition, DC polarization was examined to determine inhibition mechanism at concentratio...
متن کاملTurmeric extract as a biocompatible inhibitor of mild steel corrosion in 3.5% NaCl solution
Corrosion inhibitory impacts of turmeric with concentrations of 200-800 ppm on the electrochemical behavior of mild steel were studied in the medium of NaCl 3.5% using several techniques such as electrochemical impedance spectroscopy (EIS) and polarization. Scanning electron microscopy (SEM) was used for analyzing the surface of mild steel after 24 hours of immersion in the electrolyte solution...
متن کاملInvestigation on the corrosion behaviour of 420 welding martensitic steel with the ER308L, ER309L and ER420 fillers studied in 3.5% NaCl solution with and without CO2
In this research 420 martensitic stainless steel welded with the ER308L, ER309L and ER420 fillers by GTAW method. The corrosion properties of the samples has been studied in 3.5% NaCl solution with and without CO2. Potentiodynamic polarization used to obtain the ER308L and ER309L have the best corrosion properties. In addition the welding process makes the 420 HAZ zone to be sensitized. The pi...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Materials Science and Chemical Engineering
سال: 2014
ISSN: 2327-6045,2327-6053
DOI: 10.4236/msce.2014.210008