Corrosion Behavior of X80 Steel with Coupled Coating Defects under Alternating Current Interference in Alkaline Environment
نویسندگان
چکیده
منابع مشابه
Corrosion Behavior of X80 Steel with Coupled Coating Defects under Alternating Current Interference in Alkaline Environment
The corrosion behavior of X80 steel in the presence of coupled coating defects was simulated and studied under the interference of alternating current (AC) in an alkaline environment. The results from electrochemical measurements showed that the electrode potential of the coating defect with the smaller exposed area was lower than that with the larger area, which indicated that the steel with t...
متن کاملEffect of Alternating Current on the Cathodic Protection and Interface Structure of X80 Steel
This study employs potential-monitoring techniques, cyclic voltammetry tests, alternating current (AC) voltammetry methods, and surface characterization to investigate the AC corrosion of cathodically protected X80 pipeline steel. In a non-passive neutral solution at pH 7.2, a sufficiently negative potential completely protects steel at an AC current density of 100 A/m². In an alkaline solution...
متن کاملRelationship between Dissolved Oxygen and Corrosion Characterization of X80 Steel in Acidic Soil Simulated Solution
The relationship between dissolved oxygen (DO) and corrosion behavior of X80 steel in acidic soil simulated solution was studied by potentiodynamic polarization curves, electrochemical impedance spectroscopy (EIS), scanning Kelvin probe technique (SKP) and X-ray diffraction (XRD). Results showed that the presence of DO accelerated the cathodic process of corrosion for X80 steel in the acidic so...
متن کاملCorrosion of Cold Spray Deposited Copper Coating on Steel Substrates
The corrosion behavior of copper cold spray coatings on a carbon steel substrate was compared to that of commercially available wrought copper under the conditions anticipated in a nuclear waste repository. Corrosion potential and linear polarization resistance measurements were conducted over 90 d to 120 d in 3.0 mol/L NaCl under anoxic (1) and oxygenated-toanoxic (2) conditions to simulate th...
متن کاملCorrosion Steel Inspection under Steel Plate Using Pulsed Eddy Current Testing
Pulsed eddy current inspection techniques were derived from the conventional eddy current testing technology, based on the fundamental principle of an eddy current coil, but using periodic ultrasound pulses. The authors first introduce the principle of pulsed eddy current inspection and some experimental measurement results using pulsed eddy current equipment. This technology can be applied to ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Materials
سال: 2017
ISSN: 1996-1944
DOI: 10.3390/ma10070720