Corrosion behavior of the weld joint of X80 pipeline steel in an acidic red soil
نویسندگان
چکیده
منابع مشابه
Relationship between Dissolved Oxygen and Corrosion Characterization of X80 Steel in Acidic Soil Simulated Solution
The relationship between dissolved oxygen (DO) and corrosion behavior of X80 steel in acidic soil simulated solution was studied by potentiodynamic polarization curves, electrochemical impedance spectroscopy (EIS), scanning Kelvin probe technique (SKP) and X-ray diffraction (XRD). Results showed that the presence of DO accelerated the cathodic process of corrosion for X80 steel in the acidic so...
متن کاملEffect of Heat Input of Submerged Arc Welding Process on the Corrosion Behavior of API X42 Gas Pipeline Steel Weld Joint
The effect of heat input of submerged arc welding process on the corrosion bahavior of weld metal of API X42 gas pipeline steel weld joint was investigated. For this purpose, 6 annealed sheets of 15mm thickness were prepared from the X42 microalloyed steel. Submerged arc welding process with varying heat input of 37.8, 18.9 and 12.6 kJ/mm was used for joint welding. Then potentiodynamic polariz...
متن کاملEffect of Heat Input of Submerged Arc Welding Process on the Corrosion Behavior of API X42 Gas Pipeline Steel Weld Joint
The effect of heat input of submerged arc welding process on the corrosion bahavior of weld metal of API X42 gas pipeline steel weld joint was investigated. For this purpose, 6 annealed sheets of 15mm thickness were prepared from the X42 microalloyed steel. Submerged arc welding process with varying heat input of 37.8, 18.9 and 12.6 kJ/mm was used for joint welding. Then potentiodynamic polariz...
متن کاملCorrosion Behavior of X80 Steel with Coupled Coating Defects under Alternating Current Interference in Alkaline Environment
The corrosion behavior of X80 steel in the presence of coupled coating defects was simulated and studied under the interference of alternating current (AC) in an alkaline environment. The results from electrochemical measurements showed that the electrode potential of the coating defect with the smaller exposed area was lower than that with the larger area, which indicated that the steel with t...
متن کاملInvestigation on Effect of Heat Input on the Corrosion Behavior of Hadfield Steel Weld Joints in SMAW Process
In this investigation, the effect of heat input of SMAW process on the corrosion behavior of Hadfield steel weld joints was investigated. For this purpose, 4 annealed sheets with thickness 25 mm prepared from Hadfield steel and then welding applied by SMAW process with 6.75 and 11.25 kJ/mm heat input values. For corrosion behavior evaluation of base metal and weld metal areas, potentiodynamic p...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Materials Research Express
سال: 2020
ISSN: 2053-1591
DOI: 10.1088/2053-1591/ab71c8