Corrosion and Hydrogen Absorption of Carbon Steels in CO2 Environment.
نویسندگان
چکیده
منابع مشابه
Effect of Chromium on Corrosion Behavior of P110 Steels in CO2-H2S Environment with High Pressure and High Temperature
The novel Cr-containing low alloy steels have exhibited good corrosion resistance in CO₂ environment, mainly owing to the formation of Cr-enriched corrosion film. In order to evaluate whether it is applicable to the CO₂ and H₂S coexistence conditions, the corrosion behavior of low-chromium steels in CO₂-H₂S environment with high pressure and high temperature was investigated using weight loss m...
متن کاملPreparation of Graphene-amine Nanofluid for Absorption of Carbon Dioxide (CO2) and Hydrogen Sulfide (H2S) from a Natural Gas Stream in a Wetted Wall Column
In this study, it was shown that how CO2 and H2S were removed from a natural gas stream, using a nanofluid containing nanoporous graphene in Diehanolamine (DEA). Before running the experiments, the appropriate values were chosen for the nanosheet dosage and the liquid and gas flow rates in the absorption experiments, which were performed in a laboratory scale wetted wall column. In the expe...
متن کاملCharacteristics of Hydrogen Embrittlement, Stress Corrosion Cracking and Tempered Martensite Embrittlement in High-strength Steels
Characteristics of tempered martensite embrittlement (TME), hydrogen embrittlement (HE), and stress corrosion cracking (SCC) in high-strength steels are reviewed. Often, it is important to determine unambiguously by which of these mechanisms failure occurred, in order to suggest the right actions to prevent failure recurrence. To this aim, samples made of high-strength AISI 4340 alloy steel wer...
متن کاملA Comparison of Hydrogen Embrittlement and Stress Corrosion Cracking in High Strength Steels
The purpose of this study was to compare the known behavior of hydrogen embrittled high-strength steel to the characteristics of environmentallyinduced stress corrosion failure where hydrogen is continuously generated at the specimen surface. The incubation time for the initiation of slow crack growth was accelerated by prestressing for a fixed time below the lower critical limit. These results...
متن کاملCorrosion of Carbon and Stainless Steels in Condensed Black Liquor Vapors
Condensate of black liquor vapors is known to cause corrosion in pulp mill equipment like digesters, flash tanks, storage tanks, evaporator domes, and other equipment handling black liquor condensate. This type of corrosion typically occurs in parts of equipment where the black liquor vapors can condense on a metal surface. Generally organic acids and other wood extractives in the condensate ar...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Society of Materials Science, Japan
سال: 1996
ISSN: 1880-7488,0514-5163
DOI: 10.2472/jsms.45.1186