Corrosion and Heat Resistant Materials. Development of High-performance TiAl Exhaust Valve.
نویسندگان
چکیده
منابع مشابه
Effect of Contact Pressure and Frequency on Contact Heat Transfer Between Exhaust Valve and its Seat
The hot gases produced by the internal combustion engines passes through the exhaust valve and causes high temperatures in the exhaust valve and its seat. To avoid damaging the exhaust valve, heat must be transferred from the valve to its seat during the contact they make at the opening and closing cycle. Heat transfer rate from the exhaust valve to its seat is a function of many factors. One o...
متن کاملDevelopment of Corrosion Resistant Zn-Ni-TiO2 Composite Coatings
The Zn-Ni-TiO2 composite coatings were developed on mild steel by electrodeposition method. The bath constituents (ZnSO4.6H2O, NiSO4.6H2O, TiO2, thiamine hydrochloride) and operating conditions (temperature and pH) were optimized by Hull cell method, for peak performance of the coating against corrosion. The coatings were prepare...
متن کاملHigh Strength Corrosion Resistant Metals
There are a number of ways to improve the corrosion and abrasion resistance of metals, including alloying, anodizing, nitriding and application of protective thin films. Alloying involves generating a binary phase diagram to determine the optimum composition and temperature dependence. For example, copper alloys known as “bronzes” offer high strength, abrasion resistance and high temperature co...
متن کاملTHE OXIDATION RESISTANCE OF HIGH ALUMINUM HEAT RESISTANT STEELS
Abstract: In this research, the oxidation behaviour of high Aluminum heat resistant steel (%25Cr,%20Ni,%8Al) hasbeen evaluated at the temperature range of (1000-1300ºC).The results showed that there was no countinous healinglayer on the surface of the alloy when Al increased up to %5.5 and the oxidation resistance of steel decreased due toformation of spinel oxides on the surface.By increasing ...
متن کاملCost - Effective TiAl based Materials
Because of their inherent low ductility, TiAl-based materials are difficult to fabricate, especially thin gage titanium gamma aluminide (TiAl) sheet and foil. In this paper, an innovative powder metallurgy approach for producing cost-effective thin gage TiAl sheets (with 356 mm long and 235 mm wide, and a thickness of 0.74, 1.09, 1.55, and 2.34 mm, respectively) is presented. The microstructure...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: DENKI-SEIKO[ELECTRIC FURNACE STEEL]
سال: 1996
ISSN: 0011-8389
DOI: 10.4262/denkiseiko.67.109