Correlation of Microstructure with Hardness and Wear Resistance of (Cr3C2,CrB)/Steel Surface Alloyed Materials Fabricated by High-Energy Electron Beam Irradiation
نویسندگان
چکیده
منابع مشابه
MICROSTRUCTURE, HARDNESS AND SURFACE ROUGHNESS CHARACTERIZATION OF EBM FABRICATED Ti-6Al-4V SAMPLES
Electron beam melting (EBM) is among the modern additive manufacturing processes whereby metal powders are selectively melted to produce very complicated components with superior mechanical properties. In this study, microstructure, hardness, and surface roughness of EBM fabricated Ti6Al4V samples were characterized. The results showed that the microstructure consisted of epitaxially-grown prim...
متن کاملEvaluation of hardness and wear resistance of interim restorative materials
BACKGROUND The interim restorative materials should have certain mechanical properties to withstand in oral cavity. The aim of this study was to evaluate the hardness and wear resistance of interim restorative materials. MATERIALS AND METHODS Fifteen identical rectangular shape specimens with dimensions of 2 mm × 10 mm × 30 mm were made from 7 interim materials (TempSpan, Protemp 3 Garant, Re...
متن کاملThe effect of high-energy electron beam on drawn and undrawn high density polyethylene fibers
HDPE monofilaments were obtained using different extruders and drawn by post-extruder equipments. After solidification, drawn and undrawn monofilaments (draw ratio 7:1) were irradiated with 10 MeV electron beams in air at room temperature at 25, 50, 75, 100 and 125 kGy dose ranges to induce a network structure. HDPE crosslinking was studied on the basis of gel content measurements. The fibers w...
متن کاملTreatment of Synthetic Textile Wastewater by Combination of Coagulation/Flocculation Process and Electron Beam Irradiation
Introduction: Textile wastewaters from dyeing and finishing processes are heavily polluted with dyes, textile auxiliaries and chemicals and have a broad range of pH, high COD concentration and suspended particles. In this study, the efficiency of color and turbidity removal from synthetic textile wastewater samples were investigated by combined process of coagulation/ flocculation and electron ...
متن کاملEvaluating Wear Properties of AISI 420 Martensitic Stainless Steel after Laser Transformation Hardening
As the turbine industries need to manufacture turbine blades made of martensitic stainless steel AISI 420 with high toughness and wear resistance, local laser hardening has become more and more important. In this research, surface of the samples was initially hardened by high-power pulsed laser beam; then, optimum parameters of hardening were calculated and wear resistance of surface hardened s...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Metallurgical and Materials Transactions A
سال: 2007
ISSN: 1073-5623,1543-1940
DOI: 10.1007/s11661-007-9186-6