Correlation between the Mechanical and Tribological Properties of Rutile Reinforced LM27 Alloy Composite
نویسندگان
چکیده
To meet the global requirements of industry, there is a need for innovative light weight, low cost, eco-friendly, high quality engineering materials with superior performance at wide range temperatures. Aluminum Matrix Composites (AMCs) are lightweight isotropic properties, suitable choice modern industry. Low-cost aluminum alloys reinforced minerals have found special place in automotive industry manufacture automobile parts. Rutile particles improve mechanical properties matrix, making it attractive structural applications as well providing greater wear resistance to composite during sliding. In present studies, rutile mineral LM27 alloy was developed through stir casting route 6, 9 and 12 wt.% reinforcements. study effect particle size on tribological samples fine-sized (50–75 μm) coarse-sized (106–125 were prepared From results experiment, that hardness, compressive strength increase increasing addition. The worn surface re-groove new restored sliding help oxide films. analysis fractured clearly indicates energy dispersive X-ray spectroscopy (EDS) volume fraction particles, porosity increases, which could be main reason compression failure material.
منابع مشابه
Evaluation of Mechanical and Tribological Properties of Glass/Carbon Fiber Reinforced Polymer Hybrid Composite
Polymer matrix composites used in different industrial applications due to their enhanced mechanical properties and lightweight. However, these materials are subjected to friction and wear situations in some industrial and automobile applications. Therefore, there is a need to investigate the wear properties of polymer matrix composite materials. This article emphasizes the dry abrasive wear be...
متن کاملMechanical and Tribological Behavior of Aluminum Alloy LM13 Reinforced with Titanium Dioxide Metal Matrix Composites
In the present research work physical, mechanical and tribological behavior of Aluminum (Al) alloy LM13 reinforced with Nano-sized Titanium Dioxide (TiO2) particulates were fabricated, mechanical and tribological properties were investigated. The amount of nano TiO2 particulates in the composite was added from 0.5% to 2% in 0.5 weight percent (wt %) increments. The Al-LM13-TiO2 Metal Matrix Com...
متن کاملdetermination of some physical and mechanical properties red bean
چکیده: در این تحقیق، برخی خواص فیزیکی و مکانیکی لوبیا قرمز به-صورت تابعی از محتوی رطوبت بررسی شد. نتایج نشان داد که رطوبت بر خواص فیزیکی لوبیا قرمز شامل طول، عرض، ضخامت، قطر متوسط هندسی، قطر متوسط حسابی، سطح تصویر شده، حجم، چگالی توده، تخلخل، وزن هزار دانه و زاویه ی استقرار استاتیکی در سطح احتمال 1 درصد اثر معنی داری دارد. به طوری که با افزایش رطوبت از 54/7 به 12 درصد بر پایه خشک طول، عرض، ضخام...
15 صفحه اولBoron nitride nanotube reinforced hydroxyapatite composite: mechanical and tribological performance and in-vitro biocompatibility to osteoblasts.
This study proposes boron nitride nanotube (BNNT) reinforced hydroxyapatite (HA) as a novel composite material for orthopedic implant applications. The spark plasma sintered (SPS) composite structure shows higher density compared to HA. Minimal lattice mismatch between HA and BNNT leads to coherent bonding and strong interface. HA-4 wt% BNNT composite offers excellent mechanical properties-120%...
متن کاملmodification of nanoclay for improving the physico-mechanical properties of dental adhesives
هدف اصلی این مطالعه تهیه یک سامانه نوین چسب عاجی دندانی بر پایه نانورس پیوند شده با پلی متاکریلیک اسید، نانورس پیوند شده با پلی اکریلیک اسید، مخلوط نانوسیلیکا و نانورس پیوند شده با پلی متاکریلیک اسید، مخلوط نانوسیلیکا و نانورس پیوند شده با پلی اکریلیک اسید و نانورس پیوند شده با کیتوسان اصلاح شده با گلایسیدیل متاکریلات است. پیوند پلی متاکریلیک اسید و پلی اکریلیک اسید بر ری سطح نانورس در حضور و ...
ذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Lubricants
سال: 2022
ISSN: ['2075-4442']
DOI: https://doi.org/10.3390/lubricants10100251