Correction to: Stimulation of Spark-Plasma Sintering of Mixtures of Oxide–Non-oxide Components by Adding a Solid Solution of TaB2–NbC and through a Nickel Melt in Mixtures of Metal Powders

The effects of mixtures Ni–Ta and Ni–Zr powders combined with sintered solid solution TaB2 –NbC during spark-plasma sintering compositions at a pressing loading 60 MPa in the range 1200 – 1600°C on phase composition, percent content Ti, Ta, Zr sialon; microstructure; grain sizes crystalline phases; relative density; linear shrinkage; physical-mechanical properties; correlation elasticity modulus fracture toughness mullite–β–SiAlON–TiC mullite–β–SiAlON–c-ZrO2 samples are shown. Synthesized β-SiAlON TiC characterized by extensive crystallization TiC. c-ZrO2 1400°C –NbC, 1800°C, show (Nb,Ta)C, B phases. microstructure is crystalline, partially nonuniform, almost completely sintered. Sintered Ta additives mullitization; active β-SiAlON, B, Ni(Nb,Ta); varying NiTi, NiTa, NiZr, NiZr2 phases 1600°C. microstructures ceramic additive more uniformly densely Particles NiTi NiTa packed, unlike particles NiZr additive. Sintering proceeds extensively formation polydisperse grains. Samples growth larger values properties, higher crack resistance, better