Correction to: Correlation between platinum–aluminide coating features and tensile behavior of nickel-based superalloy Rene®80
نویسندگان
چکیده
منابع مشابه
Nickel Base Superalloy Rene®80 – The Effect of High Temperature Cyclic Oxidation on Platinum-Aluminide Coating Features
Nickel base superalloy alloys are used in the manufacture of gas turbine engine components, which in use are exposed to high temperatures and corrosive environments. The platinum aluminide coatings described here have been developed to protect nickel base superalloy alloys from oxidation. In this study, the effect of cyclic oxidation, platinum layer thickness and aluminizing process on beha...
متن کاملFormation and Evaluation of Oxidation Behavior of Zirconia- Aluminide Coating on Nickel- Based Alloy
Practical applications of thermal barrier coatings with aluminide bond-coats are limited due to oxide scale spallation of the aluminide coating under applied thermal stresses. Considering the positive effects of oxygen-active elements or their oxides on the high temperature oxidation behavior, in this research zirconia was introduced into an aluminide coating. For this purpose, a Watts type bat...
متن کاملConstitutive Model Based on Dynamic Recrystallization Behavior during Thermal Deformation of a Nickel-Based Superalloy
Peng Zhang 1, Cen Yi 1, Gang Chen 1, Heyong Qin 2 and Chuanjie Wang 1,* 1 School of Materials Science and Engineering, Harbin Institute of Technology at Weihai, Weihai 264209, China; [email protected] (P.Z.); [email protected] (C.Y.); [email protected] (G.C.) 2 Central Iron & Steel Research Institute, Beijing 100081, China; [email protected] * Correspondence: [email protected]; Tel.: +86-631-568...
متن کاملCyclic oxidation behavior of uncoated and aluminum-rich nickel aluminide coated Rene-80 superalloy
In this study, aluminide coating was employed to enhance the high-temperature cyclic oxidation of Rene-80 superalloy at 950ºC. The microstructural aspects and phase constituents of samples were investigated with scanning electron microscopy (SEM) and x-ray diffraction (XRD) techniques. The result of oxidation tests showed that the weight gain in the uncoated sample was considerably higher than...
متن کاملMean vs. Life-limiting Fatigue Behavior of a Nickel-based Superalloy
The mean and the life-limiting behavior under fatigue of the nickel-based superalloy, IN100, separated (or converged) as a function of stress level and dwell loading. This behavior was related to the control of the life-limiting behavior by the smallcrack growth regime, producing its much slower response to stress level and dwell-time, relative to the mean-lifetime behavior. The lifetime probab...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Rare Metals
سال: 2019
ISSN: 1001-0521,1867-7185
DOI: 10.1007/s12598-019-01332-0