Copper Iron Conversion Coating for Solid Oxide Fuel Cell Interconnects
نویسندگان
چکیده
منابع مشابه
Electrophoretic deposition of MnCr2O4 coating for solid oxide fuel cell metallic interconnects
In the present study, Mn - Cr spinel powder was synthesized through a solid state reaction. In the next step, the electrophoretic deposition (EPD) method was used to apply the MnCr2O4 spinel, as an oxidation-resistant layer, on SUS 430 stainless steel in a potential of 300 V/cm. The coated and uncoated samples were then pre-sintered in air at 900 °C for 3 h followed by cyclic oxidation at 800 °...
متن کاملDevelopment of Copper-Ferrite Spinel Coating on AISI 430 Steel Used as Solid Oxide Fuel Cell
The bare and pre-oxidized AISI 430 pieces were screen printed by copper ferrite spinel coatings. Good bonding between the coating and the substrate was achieved by the reactive sintering process of the reduced coating. The energy dispersive X-ray spectroscopy (EDS) analysis revealed that the scale is a double layer consisting of a chromia-rich subscale and an outer Cu/Fe-rich spinel. The result...
متن کاملDevelopment of Copper-Ferrite Spinel Coating on AISI 430 Steel Used as Solid Oxide Fuel Cell
The bare and pre-oxidized AISI 430 pieces were screen printed by copper ferrite spinel coatings. Good bonding between the coating and the substrate was achieved by the reactive sintering process of the reduced coating. The energy dispersive X-ray spectroscopy (EDS) analysis revealed that the scale is a double layer consisting of a chromia-rich subscale and an outer Cu/Fe-rich spinel. The result...
متن کاملCo3O4 spinel protection coating for solid oxide fuel cell interconnect application
In the present study, electrophoretic deposition (EPD) method in different electric fields (30 – 300 V / cm) was used to apply Co3O4 spinel coating to SUS 430 as SOFC interconnect. The coated and uncoated specimens were pre-sintered in air at 800 and 900 °C for 3 h followed by cyclic oxidation at 700 and 800 °C for 500 h, respectively. X-ray diffraction analysis (XRD), Scanning Electron Microsc...
متن کاملThermal Growth Cu1.2Mn1.8O4 Spinel Coatings on Metal Interconnects for Solid Oxide Fuel Cell Applications
A novel cobalt-free Cu1.2Mn1.8O4 spinel coating is prepared and evaluated for the metal interconnect of solid oxide fuel cell. Mn-35Cu and Co-35Mn alloy coatings are deposited on 430 SS substrate and then in-situ oxidized in air at 750 ◦C for 100 h. XRD results confirm that Cu1.2Mn1.8O4 spinel with some Mn2O3 is formed, and the average thickness of the coating is 70–80 μm according to cross sec...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Power Sources
سال: 2015
ISSN: 0378-7753
DOI: 10.1016/j.jpowsour.2015.06.139