Copper Precipitation Hardened, High Strength, Weldable Steel
Steel containing 0.03% carbon, 1.35% copper and 0.84% nickel had yield strength in the 540-625 MPa (78-90 Ksi) range depending on thickness, ultimate tensile strength in the 625-690 MPa (90100 Ksi) range, and 25-30% elongation when air cooled after hot rolling. No brittle heat-affected zone was formed during manual or automatic submerged arc welding without pre-heating or postheating. The fract...
متن کاملAntibacterial Mechanism of Copper-bearing Antibacterial Stainless Steel against E.Coli
A preliminary study was made on the antibacterial mechanism of copper-bearing antibacterial stainless steels against E.coli through experiments of microbiology such as EDTA (ethylenediaminetetraacetic acid) complexing, DNA smearing and AFM (atomic force microscope) observation. It was measured that the antibacterial stainless steels showed excellent antibacterial functions with antibacterial ra...
متن کاملCorrosion of Cold Spray Deposited Copper Coating on Steel Substrates
The corrosion behavior of copper cold spray coatings on a carbon steel substrate was compared to that of commercially available wrought copper under the conditions anticipated in a nuclear waste repository. Corrosion potential and linear polarization resistance measurements were conducted over 90 d to 120 d in 3.0 mol/L NaCl under anoxic (1) and oxygenated-toanoxic (2) conditions to simulate th...
متن کاملan experimental and numerical study of ductile fracture of copper/stainless steel clad sheet in deep drawing process
this work is an attempt towards employing ductile damage criterion and finite elementsimulations for prediction of fracture initiation and evolution in deep drawing of copper/stainlesssteel clad sheets. the material mechanical properties and ductile damage parameters weredetermined through standard and notched tensile tests. the effect of some important processparameters on damage evolution wer...
متن کاملCorrosion Behavior of Stainless Steel Clad Rebar
Stainless steel clad rebar (SCR) was investigated because it may become a cost-effective means of controlling corrosion in concrete under very aggressive environments. Sound SCR (316L cladding) resisted corrosion in saturated Ca(OH)2 solution (SCS) with up to 5 wt% chloride. Cladding breaks on SCR induced significant corrosion of exposed underlying CS in SCS with only 1 wt% chloride. A computer...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Industrial & Engineering Chemistry
سال: 1913
ISSN: 0095-9014,1943-2968
DOI: 10.1021/ie50059a004