Controlling Fe nanocrystallization in amorphous Fe86Zr7Cu1B6 by linear varying current Joule heating
نویسندگان
چکیده
منابع مشابه
KINETICS OF -Fe NANOCRYSTALLIZATION IN Fe55Cr18Mo7B16C4 BULK AMORPHOUS ALLOY
Abstract: In this research work, crystallization kinetics of Fe55Cr18Mo7B16C4 alloy was evaluated by X-ray diffraction, TEM observations and differential scanning calorimetric tests. In practice, crystallization and growth mechanisms were investigated using DSC tests in four different heating rates. Results showed that a two -step crystallization process occurred in the alloy in which - Fe phas...
متن کاملControlling the crystallization and magnetic properties of melt-spun Pr2Fe14BÕa-Fe nanocomposites by Joule heating
Pr2Fe14B/a-Fe based nanocomposites have been prepared through crystallization of melt-spun amorphous Pr7Tb1Fe85Nb0.5Zr0.5B6 ribbons by means of ac Joule heating while simultaneously monitoring room-temperature electrical resistance R. The R value shows a strong variation with respect to applied current I, and is closely related to the amorphous-to-nanocrystalline phase transformation. The curve...
متن کاملNanocrystallization in Co67Cr7Fe4Si8B14 Amorphous Alloy Ribbons
The nanocrystallization of Co67Fe4Cr7Si8B14 amorphous ribbons which prepared by planar flow melt spinning process (PFMS) was investigated. Crystallization of the ribbons was studied by differential thermal analysis (DTA), X-ray diffraction (XRD) and transmission electron microscopy (TEM). The DTA result of amorphous ribbon at heating rate of 10˚C/min showedoccurrence of phase transitions in two...
متن کاملEffect of Joule-Heating Annealing on Giant Magnetoimpedance of Co64Fe4Ni2B19-xSi8Cr3Alx (x = 0, 1 and 2) Melt-Spun Ribbons
In this work, we have studied the influence of dc joule-heating thermal processing on the structure, magnetoimpedance (MI) and thermal properties of Co64Fe4Ni2B19-xSi8Cr3Alx (x = 0, 1, and 2) rapidly solidified melt-spun ribbons. The nanocrystallization process was carried out by the current annealing of as-spun samples at various current densities. As-spun and joule-heated samples were studied...
متن کاملNANOCRYSTALLIZATION MECHANISMS OF Fe52Cr18Mo7B16C4Nb3 BULK AMORPHOUS STEEL
Crystallization kinetics of Fe52Cr18Mo7B16C4Nb3 alloy was evaluated using X-ray diffraction, differential scanning calorimetric (DSC) tests and TEM observations in this research work. In effect, crystallization and growth mechanisms were investigated using DSC tests in four different heating rates (10, 20, 30, 40 K/min) and kinetic models (i.e. Kissinger- Starink, Ozawa, and Matusita methods). ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Applied Physics Letters
سال: 2000
ISSN: 0003-6951,1077-3118
DOI: 10.1063/1.1290049