Controlled Radical Polymerization in Emulsion

Pickering emulsion templated interfacial atom transfer radical polymerization for microencapsulation.

This Article describes a new microencapsulation method based on a Pickering emulsion templated interfacial atom transfer radical polymerization (PETI-ATRP). Cationic LUDOX CL nanoparticles were coated electrostatically with an anionic polymeric ATRP initiator, poly(sodium styrene sulfonate-co-2-(2-bromoisobutyryloxy)ethyl methacrylate) (PSB), prepared by radical copolymerization of sodium styre...

Nonspherical nanoparticles with controlled morphologies via seeded surface-initiated single electron transfer radical polymerization in soap-free emulsion.

This work reports a facile novel approach to prepare asymmetric poly(vinylidene fluoride)/polystyrene (PVDF/PS) composite latex particles with controllable morphologies using one-step soap-free seeded emulsion polymerization, i.e., surface-initiated single electron transfer radical polymerization (SET-RP) of styrene (St) at the surface of PVDF seed particles. It was observed that the morphology...

Block and Graft Copolymerization by Controlled/Living Radical Polymerization Methods

Multiphase Polymer Dispersions and Nanocomposites by Catalytic/Free Radical Emulsion Polymerization

Emulsion polymerization is one of the most important and versatile polymerization processes. About 10 million tonnes of polymer latices are produced annually for a variety of applications, such as coatings and paints. A key step in most applications is film formation upon evaporation of the dispersing medium, rendering aqueous dispersions particularly environmentally benign. Polymer dispersions...

Submicron polyethylene particles from catalytic emulsion polymerization.

Particles of linear polyethylene (M(n) = (2-3) x 10(3) g x mol(-)(1); M(w)/M(n) = 2-4) obtained by catalytic emulsion polymerization of ethylene possess a nonspherical, lentil-like shape with an average aspect ratio of ca. 10 and diameters from 30 to >300 nm, as determined by TEM and AFM. The particle structure results from a stacking of the lamellae along the one shorter axis of the lentils (i...