Control of Shrinkage by Loading during Sintering of Water-atomized High-speed-steel Powder Compacts.
نویسندگان
چکیده
منابع مشابه
Lubricant Pyrolysis During Sintering of Powder Metallurgy Compacts
The chemistry surrounding the pyrolysis of N,NЈ-ethylenebisstearimide (EBS) compacted with iron powder is described for the first time. Heat treatment is carried out in a 5 vol pct hydrogen atmosphere (balance nitrogen) over the 100 °C to 850 °C range. The exhaust from the furnace is monitored by Fourier transform infrared and dispersive ultraviolet absorption spectroscopy; condensable material...
متن کاملcontrol of the optical properties of nanoparticles by laser fields
در این پایان نامه، درهمتنیدگی بین یک سیستم نقطه کوانتومی دوگانه(مولکول نقطه کوانتومی) و میدان مورد مطالعه قرار گرفته است. از آنتروپی ون نیومن به عنوان ابزاری برای بررسی درهمتنیدگی بین اتم و میدان استفاده شده و تاثیر پارامترهای مختلف، نظیر تونل زنی(که توسط تغییر ولتاژ ایجاد می شود)، شدت میدان و نسبت دو گسیل خودبخودی بر رفتار درجه درهمتنیدگی سیستم بررسی شده اشت.با تغییر هر یک از این پارامترها، در...
15 صفحه اولSintering and Foaming of Barium Silicate Glass Powder Compacts
The manufacture of sintered glasses and glass-ceramics, glass matrix composites, and glass-bounded ceramics or pastes is often affected by gas bubble formation. Against this background, we studied sintering and foaming of barium silicate glass powders used as SOFC sealants using different powder milling procedures. Sintering was measured by means of heating microscopy backed up by XPD, differen...
متن کاملMicrostructural evolution of mullite during the sintering of kaolin powder compacts
Kaolin particles are usually ̄aky in shape. In the present study, kaolin powder compacts were prepared by applying the diepressing technique. The kaolin ̄akes tend to lie down on the plane which is perpendicular to the die-pressing direction. The powder compact thus shows anisotropic shrinkage after ®ring. A series of phase transformations take place as the kaolin is ®red at elevated temperatur...
متن کاملSpark Plasma Co-Sintering of Mechanically Milled Tool Steel and High Speed Steel Powders
Hot work tool steel (AISI H13) and high speed steel (AISI M3:2) powders were successfully co-sintered to produce hybrid tool steels that have properties and microstructures that can be modulated for specific applications. To promote co-sintering, which is made difficult by the various densification kinetics of the two steels, the particle sizes and structures were refined by mechanical milling ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Society of Powder and Powder Metallurgy
سال: 1994
ISSN: 0532-8799,1880-9014
DOI: 10.2497/jjspm.41.1134