Constrained Transverse Cracking in Composite Laminates
نویسندگان
چکیده
منابع مشابه
Cracking in brittle laminates from concentrated loads
A study is made of the crack resistance of multilaminates consisting of brittle layers interleaved with compliant interlayers and bonded to compliant substrates. Specific attention is paid to flexure-generated radial cracks in the undersurfaces of individual glass layers from concentrated loads applied at the top surfaces. A proposed condition for acceptance of such multilayer systems is that r...
متن کاملA new cohesive model for simulating delamination propagation in composite laminates under transverse loads
A new cohesive model for simulating delamination propagation in composite laminates under transverse loads. Running title: A new cohesive model for simulating delamination propagation in composite laminates 2 Abstract In this paper, we propose a new cohesive model to stably and accurately simulate the delamination propagations in composite laminates under quasi-static and low-velocity impact tr...
متن کاملA Statistical Approach to Evaluate the Effect of Manufacturing Quality on Transverse Cracking in Cross Ply Laminates
Most studies of the effects of manufacturing defects such as voids have focused on composite strength properties, e.g. the interlaminar strength [1]. The current study investigates how irregularities in the manufacturing process affect progressive damage in the subcritical regime. This effort is along the lines of a broader strategy for performance evaluation of composites coined as defect dama...
متن کاملOn the Effect of Residual Stresses on the Transverse Cracking in Cross-ply Carbon-polyetherimide Laminates Proefschrift
Two themes form the basis of this study on fibre reinforced laminated composites: namely 'thermal residual stress' and 'transverse cracking'. Thermal residual stresses are inherent to any composite structure and are internal stress within the structure that form during manufacture. Their formation arises from the difference in coefficient of thermal expansion of the fibre and the matrix. These ...
متن کاملComputational Implementation of a Thermodynamically Based Work Potential Model for Progressive Microdamage and Transverse Cracking in Fiber-reinforced Laminates
A continuum-level, dual internal state variable, thermodynamically based, work potential model, Schapery Theory, is used capture the effects of two matrix damage mechanisms in a fiber-reinforced laminated composite: microdamage and transverse cracking. Matrix microdamage accrues primarily in the form of shear microcracks between the fibers of the composite. Whereas, larger transverse matrix cra...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Advanced Composites Letters
سال: 1995
ISSN: 2633-366X,2633-366X
DOI: 10.1177/096369359500400201