Conduction in Mn substituted Ni-Zn ferrites
نویسندگان
چکیده
منابع مشابه
Enhancement of Néel temperature and electrical resistivity of Mn–Ni–Zn ferrites by Gd3+ substitution
Structural, magnetic, and dielectric properties of various Mn0.5Ni0.1Zn0.4Fe2−xGdxO4 sintered at 1200 ◦C were investigated thoroughly. The samples were synthesized by standard solid state reaction technique. The crystal structure was characterized by X-ray diffraction (XRD), which has confirmed the formation of single phase spinel structure. Bulk density, average grain size and initial permeabi...
متن کاملElectrical and magnetic properties of Mn-Ni-Zn ferrites processed by citrate precursor method
MnxNi0.5 _ xZn0.5Fe2O4, (x = 0.05, 0.1, 0.2, 0.3, 0.4) ferrites synthesized by the citrate precursor method are investigated in the present work. Compositional variation of AC resistivity is studied and values up to 10 times greater than those for samples prepared by the conventional ceramic method are observed. It is found that resistivity decreases with increase in Mn concentration except for...
متن کاملTemperature dependence of core loss in cobalt substituted Ni-Zn-Cu ferrites
The temperature dependence of core loss in cobalt substituted Ni-Zn-Cu ferrites was investigated. Co ions are known to lead to a compensation of the magnetocrystalline anisotropy in Ni-Zn ferrites, at a temperature depending on the cobalt content and the Ni / Zn ratio. We observed similar behaviour in Ni-Zn-Cu and it was found that the core loss goes through a minimum around this magneto-crysta...
متن کاملImprovement of the magnetic properties for Mn–Ni–Zn ferrites by rare earth Nd3+ ion substitution
Single spinel phases of Mn0.5Ni0.1Zn0.4Nd x Fe2- x O4 ferrite samples (x = 0.0, 0.01, 0.02, 0.05, 0.075, and 0.1) have been prepared by ceramic method and the composition dependence of the physical and magnetic properties has been investigated. SEM micrographs and EDX analysis revealed that there is no considerable effect for the Nd(3+) ion substitution on the average grain size or porosity, wh...
متن کاملInterfacial Dielectric Losses in Co-Doped Ni-Zn Ferrites
The temperature and fresuency dependence of tg8 and E' for Nk ~Ztb ferrites was studied in the 10'lo6 Hz frequency range and 20-200°C temperrhrre tange. The experimental curves exhibit aspects very dependent of composition. To verify Ulat interfacial losses, expected to appear in this type of system are compatible with the experimental results a calculation of the dielectric permittivity and di...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Bulletin of Materials Science
سال: 1996
ISSN: 0250-4707,0973-7669
DOI: 10.1007/bf02744824