Compressive strength optimization of metakaolin‐based geopolymer by central composite design
نویسندگان
چکیده
منابع مشابه
Factors Influencing Compressive Strength of Geopolymer Concrete
To study effects of several factors on the properties of fly ash based geopolymer concrete on the compressive strength and also the cost comparison with the normal concrete. The test variables were molarities of sodium hydroxide(NaOH) 8M,14M and 16M, ratio of NaOH to sodium silicate (Na2SiO3) 1, 1.5, 2 and 2.5, alkaline liquid to fly ash ratio 0.35 and 0.40 and replacement of water in Na2SiO3 s...
متن کاملFormation of Poly(vinylidenefluoride) Nanofibers: Part I Optimization by Using of Central Composite Design
Poly(vinylidene fluoride) (PVDF) nanofibers were prepared via electrospinning process. Several different factors influence on this process and application of experimental design for its optimization is of great importance. The central composite design (CCD) was used for planning and optimizing of the experiments and also, the analysis of variance (ANOVA) was employed for the statistical va...
متن کاملEnhancing Mechanical Strength of Inorganic Geopolymer by Using Phenol Resin
The effect of organic phenol on the compressive and flexural strength of a metakaolin based geopolymer is studied. It was found that 12 wt% phenol resins can increase the compressive and flexural strength by 30% and 65% respectively. In addition, the reinforcing effect of phenol resin is higher in Na-PS and Na-PSS type geopolymers rather than Na-PSDS. Two distinct endothermic peaks were detecte...
متن کاملApplication of Central Composite Design for Optimization of Coacervative Extraction of Cu(II) Using Anionic Surfactant
The aim of this work was to develop a new and simple coacervative extraction method for the preconcentration and spectrophotometric determination of Cu(II) in water samples. Dithizone was used as the chelating agent while an anionic surfactant, namely sodium dodecyl sulfate (SDS), was used as extracting agent at room temperature. Central composite design (CCD) based on response surface methodol...
متن کاملModeling and Optimization of Mechanical Properties of PA6/NBR/Graphene Nanocomposite Using Central Composite Design
Thermoplastic elastomer of PA6/NBR reinforced by various nanoparticles have wide application in many industries. The properties of these materials depend on PA6, NBR, and nanoparticle amount and characteristics. In this study, the simultaneous effect of NBR and graphene nanoparticle content on mechanical, thermal properties, and morphology of PA6/NBR/Graphene nanocomposites investigated by Cent...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Chemical Data Collections
سال: 2021
ISSN: 2405-8300
DOI: 10.1016/j.cdc.2020.100636