Compressive Deformation Properties and Microstructures in the Superplastic Y-TZP
نویسندگان
چکیده
منابع مشابه
Superplastic deformation induced by cyclic hydrogen charging
Deformation under the combined action of external stress and cyclic hydrogen charging/discharging is studied in a model material, titanium. Cyclic charging with hydrogen is carried out at 860 °C, which repeatedly triggers the transformation between hydrogen-lean -Ti and hydrogen-rich -Ti. Due to bias from the externally applied tensile stress, the internal mismatch strains produced by this isot...
متن کاملEffect of Sintering Profiles on the Properties and Ageing Resistance of Y-tzp Ceramic
A commercially available Y-TZP ceramic powder was fabricated under four different sintering profiles in order to investigate the effects of conventional single-stage sintering (SSS) with dwell times of 1 min and 2 h, respectively, compared with two-stage sintering (TSS), on the physical and mechanical properties of Y-TZP. Sintering was performed up to 1400 o C at a ramp rate of 10 o C/min. It w...
متن کاملThe Effect of Cerium Oxide Addition on the Properties and Behavior of Y-TZP
The effects of CeO2 addition on the sintering behavior and mechanical properties of Y-TZP have been investigated over a wide sintering regime by pressureless sintering. It has been revealed that small additions of CeO2 (0.3-1.0 wt%) to Y-TZP were beneficial in enhancing the mechanical properties and hydrothermal ageing resistance of Y-TZP. Sintered samples were used to evaluate the bulk density...
متن کاملAchieving microstructures prone to superplastic deformation in an Al - Zn - Mg - Cu alloy by equal channel angular pressing
An Al-Zn-Mg-Cu alloy without Sc or Zr additions was subjected to overaging and processing by equal channel angular pressing, obtaining a grain size of ∼160 nm and a fraction of high-angle boundaries of 56%. The high elongations attained at high strain rate (10-10 s) and low test temperature (250-300 oC) are attributed to the formation of new recrystallized grains, ∼500 nm in size, during heatin...
متن کاملSuperplastic deformation in carbonate apatite ceramics under constant compressive loading for near-net-shape production of bioresorbable bone substitutes.
To produce carbonate apatite (CAP) ceramics with the desired complex shapes using superplastic deformation, deformation behavior of CAP ceramics under constant loading as well as physical properties after deformation were evaluated. Sintered CAP ceramics were plastically deformed in an electric furnace attached to a universal hydraulic testing machine under a constant load. CAP ceramics subject...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Ceramic Association, Japan
سال: 1986
ISSN: 1884-2127,0009-0255
DOI: 10.2109/jcersj1950.94.1092_721