Compression Deformation Behavior and Processing Map of Pure Copper
نویسندگان
چکیده
منابع مشابه
Deformation Mechanisms in Pure and Alloyed Copper Films
In this work, the evolution of microstructure and the thermo-mechanical behavior of co pper and dilute copper alloy thin films was investigated. 0.3 to 2.0 μm thick film s were deposited by magnetron sputtering under ultra high vacuum conditions onto diffusion-barrier coated silicon substrates and subjected to wafer curvature measurements. Pure copper films annealed in ultra high vacuum exhibit...
متن کاملGrain Size Effect on the Hot Deformation Processing Map of AISI 304 Austenitic Stainless Steel
In this study, the hot deformation processing map of AISI 304 austenitic stainless steel in two initial grain sizes of 15 and 40 μm was investigated. For this purpose, cylindrical samples were used in the hot compression test at the temperature range of 950-1100 °C and the strain rate of 0.005-0.5% s-1. At first, the relationship between the peak stress and Zener-Hollomon parameter w...
متن کاملInvestigation on Hot Deformation Behavior and Hot Processing Map of BSTMUF601 Super-Alloy
Abstract: Isothermal compression tests of BSTMUF601 super-alloy in the temperature range of 950 ̋C–1200 ̋C and at the strain rates of 0.2 s ́1, 5 s ́1, 10 s ́1 were performed on a Gleeble-1500D thermo-mechanical simulator. Based on the hyperbolic sine function, the unified constitutive equations and hot processing maps during the hot deformation process were established. The flow stress predicted by...
متن کاملPlastic Deformation in Laser-induced Shock Compression of Monocrystalline Copper
Copper monocrystals were subjected to shock compression at pressures of 10-60 GPa by a short (3 ns initial) duration laser pulse. Transmission electron microscopy revealed features consistent with previous observations of shock-compressed copper, albeit at pulse durations in the us regime. The results suggest that the defect structure is generated at the shock front. A mechanism for dislocation...
متن کاملEVALUATING HOT DEFORMATION BEHAVIOR OF W360 TOOL STEEL BY HOT COMPRESSION TEST
In this research, the hot deformation behavior of W360 tool steel was investigated using hot compression test at 1000-1200°C and strain rates of 0.001, 0.01, 0.1, and 1 s-1. According to the results, dynamic recrystallization was found the most important restoration factor of this alloy during hot deformation. Recrystallization was enhanced with an increase in temperature and strain rate. Also,...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Strength of Materials
سال: 2016
ISSN: 0039-2316,1573-9325
DOI: 10.1007/s11223-016-9743-6