Composition Distribution on Zn-Ni Alloy Plating with Surfactant.
نویسندگان
چکیده
منابع مشابه
A Novel Electrodeposition Process for Plating Zn-Ni-Cd Alloys
Zn-Ni-Cd alloy was electrodeposited from an alkaline electrolytic bath under potentiostatic conditions. Bath analyses using a pH concentration diagram reveal that addition of a complexing agent is essential to maintain the bath stability. Introduction of a low concentration of CdSO4 reduces the anomalous nature of the Zn-Ni deposit. Deposits obtained from the electrolytic bath which contains 60...
متن کاملElectroless Nickel Plating on Magnesium Alloy
he inherent lightness and good strength-to-weight ratio of T magnesium has focused attention on increasing applications in aerospace and allied fields. Its density is two thirds that of aluminum-a conventional structure material for aerospace. Magnesium has one drawback: It is prone to atmospheric corrosion. Further, because of its high chemical affinity for aqueous solutions, it is categorized...
متن کاملEffect of heat treatment on structure and properties of multilayer Zn-Ni alloy coatings
Composition modulated multilayer alloy (CMMA) coatings of Zn-Ni were electrodeposited galvanostatically on mild steel (MS) for enhanced corrosion protection using single bath technique. Successive layers of Zn-Ni alloys, having alternately different composition were obtained in nanometer scale by making the cathode current to cycle between two values, called cyclic cathode current densities (CC...
متن کاملRecovery of Cu, Zn, Ni and Cr from Plating Sludge by Combined Sulfidation and Oxidation Treatment
The selective recovery of heavy metals of Cu, Zn, Ni and Cr from a mixed plating sludge by sulfidation and oxidation treatment was targeted in this study. At first, the mixed plating sludge was simultaneously subjected to an extraction and Cu sulfidation process at pH=1.5 to dissolve heavy metals and to precipitate Cu as CuS. In the next step, the sulfidation treatment of Zn was carried out at ...
متن کاملCation Distribution in Co0.7Me0.3Fe2O4 (Me = Zn, Ni and Mn)
Co0.7Me0.3Fe2O4 (Me = Zn, Ni and Mn) were synthesized through co-precipitation method. Cationic distribution for these ferrites was proposed on the basis of magnetization measurements and available occupancy of the substituent ions into the spinel lattice. Theoretical lattice constant calculations confirm the proposed cationic distributions were the correct ones.
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Surface Finishing Society of Japan
سال: 1999
ISSN: 0915-1869,1884-3409
DOI: 10.4139/sfj.50.836