Composite Coating Prepared with Ferulic Acid to Improve the Corrosion Resistance and Blood Compatibility of Magnesium Alloy
نویسندگان
چکیده
Magnesium (Mg) alloy has been used for medical vascular stents because of its good biocompatibility and degradability, but rapid degradation poor blood compatibility limits further application. In this study, ferulic acid (FA) was conjugated onto the polydopamine (PDA) deposited Mg-Zn-Y-Nd to prepare a PDA/FA multi-functional coating with better corrosion resistance compatibility. The results suggest that possessed potential application surface modification Mg alloy.
منابع مشابه
Corrosion Resistance Enhancement of AZ91 Magnesium Alloy Using Ni-P Interlayer and Electrophoretic Deposited 3YSZ Coating
The zirconia stabilized by 3mol % Y2O3 (3YSZ) was applied onto the surface of the magnesium alloy AZ91D using electrophoretic deposition (EPD) from a non- aqueous solution. A Ni-P interlayer between the substrate and YSZ coating was also prepared by electroless plating. Finally, coatings were heat treated in control atmosphere at 400 °C. The preparation, microstructure and corrosion resistance ...
متن کاملMg-MOF-74/MgF2 Composite Coating for Improving the Properties of Magnesium Alloy Implants: Hydrophilicity and Corrosion Resistance
Surface modification on Mg alloys is highly promising for their application in the field of bone repair. In this study, a new metal-organic framework/MgF₂ (Mg-MOF-74/MgF₂) composite coating was prepared on the surface of AZ31B Mg alloy via pre-treatment of hydrofluoric acid and in situ hydrothermal synthesis methods. The surface topography of the composite coating is compact and homogeneous, an...
متن کاملInfluence of Zeolite Coating on the Corrosion Resistance of AZ91D Magnesium Alloy
The protective performance of zeolite coating on AZ91D magnesium alloy was evaluated using potentiodynamic polarisation and electrochemical impedance spectroscopy (EIS) in 0.1 M sodium chloride solution (NaCl). Electrical equivalent circuit (EEC) was developed based upon hypothetical corrosion mechanisms and simulated to correspond to the experimental data. The morphology and the chemical natur...
متن کاملImproving Corrosion Resistance and Biocompatibility of Magnesium Alloy by Sodium Hydroxide and Hydrofluoric Acid Treatments
Owing to excellent mechanical property and biodegradation, magnesium-based alloys have been widely investigated for temporary implants such as cardiovascular stent and bone graft; however, the fast biodegradation in physiological environment and the limited surface biocompatibility hinder their clinical applications. In the present study, magnesium alloy was treated by sodium hydroxide (NaOH) a...
متن کاملCorrosion Resistance Tests of Magnesium Alloy We43 after Extrusion
J. Przondziono, E. Hadasik, J.Szala, J. Wieczorek, Faculty of Materials Science and Metallurgy, The Silesian University of Technology, Katowice, Poland, W. Walke, Faculty of Biomedical Engineering, The Silesian University of Technology, Gliwice, Poland The purpose of the study was t o evaluate resistance to electrochemical corrosion of magnesium alloy WE43 after plastic working. Potentiodynamic...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Metals
سال: 2022
ISSN: ['2075-4701']
DOI: https://doi.org/10.3390/met12040545