Complex-Shaped Porous Cu Bodies Fabricated by Freeze-Casting and Vacuum Sintering

Complex-Shaped Porous Cu Bodies Fabricated by Freeze-Casting and Vacuum Sintering

Porous Cu bodies with complex shapes were fabricated by freeze-casting and vacuum sintering water-based CuO slurry. The sintered bodies showed no noticeable macroscopic defects and good shape tolerance. The interconnected pore tunnels were observed by electronic microscopy. The pore size became smaller and the porosity and volume shrinkage of sintered porous bodies decreased with the increase o...

Pore Formation Process of Porous Ti3SiC2 Fabricated by Reactive Sintering

Porous Ti3SiC2 was fabricated with high purity, 99.4 vol %, through reactive sintering of titanium hydride (TiH2), silicon (Si) and graphite (C) elemental powders. The reaction procedures and the pore structure evolution during the sintering process were systematically studied by X-ray diffraction (XRD) and scanning electron microscope (SEM). Our results show that the formation of Ti3SiC2 from ...

Deformation aspects of anisotropic-porous bodies sintering

Biomaterials by freeze casting.

The functional requirements for synthetic tissue substitutes appear deceptively simple: they should provide a porous matrix with interconnecting porosity and surface properties that promote rapid tissue ingrowth; at the same time, they should possess sufficient stiffness, strength and toughness to prevent crushing under physiological loads until full integration and healing are reached. Despite...

Freeze-Casting of Porous Biomaterials: Structure, Properties and Opportunities

The freeze-casting of porous materials has received a great deal of attention during the past few years. This simple process, where a material suspension is simply frozen and then sublimated, provides materials with unique porous architectures, where the porosity is almost a direct replica of the frozen solvent crystals. This review focuses on the recent results on the process and the derived p...