Complete Photocatalytic Mineralization of Microplastic on TiO2 Nanoparticle Film
نویسندگان
چکیده
منابع مشابه
Electrochemical actuator based on monolithic polypyrrole–TiO2 nanoparticle composite film
A polypyrrole (PPy) composite film with a pure PPy zone and a PPy–TiO2 nanoparticle composite zone in its cross-sectional direction was synthesized by direct oxidation of pyrrole successively in an electrolyte with or without TiO2 nanoparticles. The volume content of TiO2 in the composite film was tested to be lower than 0.9%. The actuator fabricated from this monolithic PPy film bends uniforml...
متن کاملPhotocatalytic inactivation of E. coli with a mesoporous TiO2 coated film using the film adhesion method.
The photocatalytic inactivation of Escherichia coli with the film adhesion method by using Degussa P25TiO2 and mesoporous TiO2 coated on glass was investigated. Monodisperse spherical mesoporous TiO2 with a morphology size of approximately 800 nm was synthesized via the sol-gel approach and coated onto glass substrates without cracking by using the doctor blade method with various amounts of po...
متن کاملPhotocatalytic Mineralization of Methylene BlueAqueous Solutions by Ag/TiO2 Nano Composite
Nanocomposite of Ag/TiO2 and nanocrystalline TiO2 were prepared by using TiCl4 as a precursor in a simple sol-gel process. The prepared photo-catalysts were characterized by X-ray diffraction (XRD), scanning electron micrographs (SEM), energy dispersive X-ray microanalysis (EDX), transmission electron microscopy (TEM) and diffuse reflectance spectroscopy (DRS). A complete and effective photocat...
متن کاملAntibacterial surfaces based on functionally graded photocatalytic Fe3O4@TiO2 core–shell nanoparticle/epoxy composites
Functionally graded epoxy composites with various concentration profiles of Fe3O4@TiO2 core–shell nanoparticles (NPs) were synthetized and characterized, with focus on their antibacterial properties. The NPs consisted of rutile, anatase, magnetite and hematite. Graded composites were produced starting with homogeneous 2 vol% to 12 vol% NPs suspensions using a magnetophorese process, leading to ...
متن کاملEffect of compressed TiO2 nanoparticle thin film thickness on the performance of dye-sensitized solar cells
In this study, dye-sensitized solar cells (DSSCs) were fabricated using nanocrystalline titanium dioxide (TiO2) nanoparticles as photoanode. Photoanode thin films were prepared by doctor blading method with 420 kg/cm2 of mechanical compression process and heat treatment in the air at 500°C for 30 min. The optimal thickness of the TiO2 NP photoanode is 26.6 μm with an efficiency of 9.01% under A...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: iScience
سال: 2020
ISSN: 2589-0042
DOI: 10.1016/j.isci.2020.101326