Competition between Fatigue Crack Growth and Wear under Rolling – Sliding Contact Condition
نویسندگان
چکیده
منابع مشابه
Analysis of Surface Crack Growth under Rolling Contact Fatigue
Understanding the fatigue crack growth phenomenon in railheads requires a study of driving forces such as the crack tip opening and sliding displacements, under repeated rolling contact. Finite element simulations, allowing elastic-plastic deformation, and mixed-mode crack growth laws were utilized to demonstrate that the fatigue crack growth rates display a minimum after a finite amount of cra...
متن کاملInvestigations of White Etching Crack (WEC) Formation under Rolling Contact Fatigue
A premature failure mode in steel rolling element bearings called white structure flaking (WSF) occurs in wind turbine gearbox bearings. WSF can occur in as little as 6-24 months of operation. WSF is associated with microstructural alterations called white etching area (WEA) and white etching cracks (WECs) that form in the ~1 mm zone beneath the contact surface. The tribological drivers for WSF...
متن کاملRolling contact fatigue in martensitic 100Cr6: subsurface hardening and crack formation
Rolling contact fatigue tests on 100Cr6 steel were carried out with a ballon-rod tester. Microstructural damage was manifested by gradual hardness changes under the subsurface, and microcracks formed adjacent to inclusions; both being evidence of plastic deformation. The hardness increase appears to be due to the development of residual stress, while the microcracks form as a result of the conc...
متن کاملFriction and Wear Behaviors of Gear Steel under Coupling of Rolling and Sliding
In this paper, the gear material 20CrMnTi was selected as the research object. Friction and wear behavior was performed on the M2000 friction and abrasion tester. The friction and wear mechanisms of 20CrMnTi steel were discussed under coupling of rolling and sliding. The results show that damage of steel-steel couples under coupling of rolling and sliding is caused by the interaction of mechani...
متن کاملEffect of Boundary Condition on Pre-Existing Crack Under Fatigue Loading
In this paper, the present investigation has been conducted keeping in mind some of the problems concerning the crack propagation direction and growth under constant loading in an inclined crack geometry. The present studies mainly focused on the development and modifications in the crack growth criterion to account the biaxial, shear loading and number of stress terms. Existing criteria for th...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Tetsu-to-Hagane
سال: 2019
ISSN: 0021-1575,1883-2954
DOI: 10.2355/tetsutohagane.tetsu-2018-138