Comparison of Hot-rolled Unalloyed Magnesium and Magnesium Alloys in terms of Biodegradability and Mechanical Properties

In this study, hot rolling is properly performed on pure magnesium and two of Zn, Ca Mn containing alloys. Biodegradability mechanical properties are investigated comparatively in their rolled state. While the average grain sizes alloys were close to each other, it was observed that Mg-1.01Zn-1.63Ca-0.30Mn alloy had higher hardness (61.5 ± 0.2 HV) at The lowest corrosion rate electrochemical test Mg-1.07Zn-0.21Ca-0.31Mn be 1.772 mm/yr. As for immersion same alloy, detected 0.054 Moreover, has highest tensile strength. Based results, ascertained hot-rolled possesses a better biodegradability compared commercially unalloyed Mg 1.01Zn-1.63Ca-0.30Mn alloy.