Comparison of Fatigue Life Cycle of Different Aluminium Alloy AA 5083 - AA6062
نویسندگان
چکیده
منابع مشابه
Laser Welding of Aluminium Alloy 5083
There are two laser welding mechanisms, keyhole mode and conduction mode. Keyhole welding is widely used because it produces welds with high aspect ratios and narrow heat affected zones. However keyhole welding can be unstable, as the keyhole oscillates and closes intermittently. This intermittent closure causes porosity due to gas entrapment. Conduction welding, on the other hand, is more stab...
متن کاملFatigue and Anisotropic behaviours of cold rolled AA1200 Aluminium Alloy
This study examines the fatigue and anisotropy behaviour of cold rolled AA1200 aluminium alloy for light weight automotive connecting rod application. Aluminium (Al) 1200 ingots were melted at temperature of 680 0C (after one hour of heating) cast in sand mould and cast samples homogenized for 6 hrs at 480 0C. The cold rolling process was carried out after homogenisation for 10, 20, 30, 40 and ...
متن کاملFatigue of Friction Stir Welded 2024-T351 Aluminium Alloy
Fatigue failure characteristics of friction stir welds in 13mm gauge 2024-T351 plate have been assessed. Failure occurred from either the weld region (nugget/flow arm) or from the material immediately surrounding the weld. Fatigue failure from the surrounding material was essentially conventional, initiating from large S-phase intermetallic particles and growing in a macroscopic mode I manner. ...
متن کاملEvaluation of continuum damage at different temperatures for aluminum-silicon alloy of engine piston within low-cycle fatigue regime
In this article, the isothermal low-cycle fatigue continuum damage in the engine piston aluminum alloy has been evaluated at different temperatures. For this objective, experimental data of low-cycle fatigue tests on standard specimens were used at 280, 350 and 425°C. Based on the continuum damage mechanics method, the fatigue damage was calculated during cyclic loading. Obtained results, inclu...
متن کاملEffect of Harmonic Vibration on Microstructure and Mechanical Properties of AA-5083-H321 Aluminum Alloy GMAW Welds
In this research, the effect of vibration at the resonant range (75 Hz) on the hardness and tensile strength of AA-5083-H321 aluminum alloy, were welded by gas metal arc welding (GMAW) investigated. Vibration forces were ranged from 850 N to 2200 N, under identical welding parameters. Tensile strength and hardness testing of welded samples were performed. After mechanical tests, the fracture su...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: International Journal of Scientific Research in Science, Engineering and Technology
سال: 2019
ISSN: 2394-4099,2395-1990
DOI: 10.32628/ijsrset196364