Comparison of Corrosion Behavior of Electrochemically Deposited Nano-Cobalt-Coated Ni Sheet
نویسندگان
چکیده
منابع مشابه
STUDY ON CORROSION BEHAVIOR OF COBALT NANO COMPOSITE COATINGS
Metal matrix nano composite coatings possess enhanced properties such as corrosion and wear resistance. This paper aims to study the corrosion behavior of pure Co and Co-BN nano composite coatings deposited with different particles concentration (5-20 g L-1) on copper substrates using electroplating technique. Morphology and elemental compositions of the coatings were investigated by means of s...
متن کاملTribological behavior of sputter-deposited MoSX/Ni coatings
AbstractSputtered MoS2 coatings have been mostly used as a solid lubricant. In this investigation, MoSx/Ni composite coatings with Ni contents varying from 0 to 22 % were deposited onto steel substrate using a DC magnetron sputter process. The MoS2/Ni ratio in the coatings was controlled by sputtering the composite targets. The composition, microstructure, and mechanical properties of the...
متن کاملProperties of Ni and Ni–Fe nanowires electrochemically deposited into a porous alumina template
The comparative analysis of the electrochemical deposition of Ni and Ni-Fe nanowires (NWs) into ordered porous alumina templates is presented. The method developed allows for obtaining NWs of 50 ± 5 nm in diameter and 25 μm in length, i.e., with an aspect ratio of 500. XRD data demonstrate the polycrystalline nature of Ni and Ni-Fe in a face-centered cubic close-packed lattice. Both fabricated ...
متن کاملCORROSION BEHAVIOR OF ELECTROLESS Ni-P/NANOZnO COATINGS
Abstract:Electroless Nickel-phosphorus (EN) coatings provide high performance in various industrial fields due to their unique properties such as excellent corrosion and wear resistance. This paper aims to study the effect of ZnO nano-particles addition on corrosion behavior of EN coatings. Various amounts of ZnO nano-particles with average diameter of 50 nm were added to hypophosphite reduced ...
متن کاملCorrosion Resistance Enhancement of AZ91 Magnesium Alloy Using Ni-P Interlayer and Electrophoretic Deposited 3YSZ Coating
The zirconia stabilized by 3mol % Y2O3 (3YSZ) was applied onto the surface of the magnesium alloy AZ91D using electrophoretic deposition (EPD) from a non- aqueous solution. A Ni-P interlayer between the substrate and YSZ coating was also prepared by electroless plating. Finally, coatings were heat treated in control atmosphere at 400 °C. The preparation, microstructure and corrosion resistance ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Chemistry
سال: 2013
ISSN: 2090-9063,2090-9071
DOI: 10.1155/2013/543676