Comparing Biocompatibility of Nanocrystalline Titanium and Titanium-Oxide with Microcrystalline Titanium
نویسندگان
چکیده
منابع مشابه
Fatigue Properties of Nanocrystalline Titanium
Fatigue resistance of nanocrystalline commercial pure titanium obtained by hydrostatic extrusion was investigated. Coarse grained titanium and Ti6Al4V alloy were used as the reference materials. The fatigue limit and fatigue life examined at constant stress amplitude, were found to increase significantly compared to those of the coarse-grained counterparts. It is suggested that the observed imp...
متن کاملNanoporous Titanium Oxide Morphologies Produced by Anodizing of Titanium
A quick and dependable technique has been developed that allows us to selectively produce anodized TiO2 in the form of nanotubes. The process employs mild chemical conditions and ambient temperature. The method can consistently produce nearly 100% surface coverage of nanotubes within 10 min of anodizing. Anodizing in relatively high pH electrolytes for 1 hour permitted us to produce nanotubes o...
متن کاملTitanium Pnictide Oxide Superconductors
In 2012, a novel superconductor BaTi2Sb2O was found in the layered titanium pnictide oxides ATi2Pn2O. A related superconductor BaTi2Bi2O was subsequently discovered in 2013. The structure of these materials consists of alternate stacking of superconducting Ti2Pn2O layers and Ba blocking layers, which is somewhat similar to high-Tc cuprates since the Ti2Pn2O layer contains an anti-CuO2-type Ti2O...
متن کاملAmorphous titanium-oxide supercapacitors
The electric capacitance of an amorphous TiO2-x surface increases proportionally to the negative sixth power of the convex diameter d. This occurs because of the van der Waals attraction on the amorphous surface of up to 7 mF/cm2, accompanied by extreme enhanced electron trapping resulting from both the quantum-size effect and an offset effect from positive charges at oxygen-vacancy sites. Here...
متن کاملThe biocompatibility of SLA-treated titanium implants.
The titanium implant surface was sandblasted with large grits and acid etched (SLA) to increase the implant surface for osseointegration. The topography of the titanium surface was investigated with scanning electron microscopy (SEM) and a profilometer. The SLA implant demonstrated uniform small micro pits (1-2 microm in diameter). The values of average roughness (R(a)) and maximum height (R(t)...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: MRS Proceedings
سال: 2013
ISSN: 0272-9172,1946-4274
DOI: 10.1557/opl.2013.804