Comparative study of Ho:Y2O3 and Ho:Y3Al5O12 transparent ceramics produced from laser-ablated nanoparticles
نویسندگان
چکیده
Ho:Y2O3 and Ho:Y3Al5O12 transparent ceramics are fabricated by vacuum sintering at 1780 °C for 20 h from laser-ablated nanopowders (Ho:Y2O3 + Al2O3) using ZrO2 TEOS as aids, respectively. The sesquioxide ceramic exhibits smaller grain size (∼5.4 μm), content of pores (down to 6 ppm) higher optical transmission (up 82.2% ∼1 μm) than the garnet one. A detailed comparative spectroscopic study two is performed. For 5I7 → 5I8 Ho3+ transition, maximum stimulated-emission cross-sections luminescence lifetimes σSE = 0.57 × 10−20 cm2 2087.1 nm τlum 10.92 ms (for ceramic) 1.70 2090.8 7.04 one) rates multiphonon relaxation determined both ceramics. ceramic, they do not exceed those single-crystals. crystal-field splitting multiplets (5I7 5I8) 12 K analyzed barycenter plot. Due its broadband emission properties, suitable mode-locked lasers emitting above 2 μm.
منابع مشابه
control of the optical properties of nanoparticles by laser fields
در این پایان نامه، درهمتنیدگی بین یک سیستم نقطه کوانتومی دوگانه(مولکول نقطه کوانتومی) و میدان مورد مطالعه قرار گرفته است. از آنتروپی ون نیومن به عنوان ابزاری برای بررسی درهمتنیدگی بین اتم و میدان استفاده شده و تاثیر پارامترهای مختلف، نظیر تونل زنی(که توسط تغییر ولتاژ ایجاد می شود)، شدت میدان و نسبت دو گسیل خودبخودی بر رفتار درجه درهمتنیدگی سیستم بررسی شده اشت.با تغییر هر یک از این پارامترها، در...
15 صفحه اولtransference of imagery: a comparative formalistic study of shakespeares hamlet and its two persian translations
هدف از این تحقیق بررسی انتقال صور خیال هملت در دو ترجمه ی فارسی آن از نظر فرمالیستی بود. برای بدست آوردن داده-های مورد نیاز، 130 نمونه استعاره، مجاز، ایهام، کنایه و پارادوکس در متن اصلی مشخص شده و سپس بر اساس مدل نیومارک (1998) برای ترجمه ی استعاره یا بطور کلی زبان مجاز با معادل های فارسی شان مقایسه گردیدند. این تحقیق بر آن بود تا روش های استفاده شده برای ترجمه هر کدام از انواع زبان مجاز ذکر شد...
15 صفحه اولNanoparticles and Fabrication of Transparent Polycrystalline Yttria Ceramics
In this thesis, we report on a process to obtain yttrium oxide nanosized particles doped with ytterbium and a sintering method that leads to transparent polycrystalline ceramics. First, nano-powder of yttria was fabricated from a precursor with transient morphology, i.d. yttrium hydroxynitrate platelets that decompose into spherical yttria nano-particles during calcination. The influence of dif...
متن کاملa comparative study of bilingual schools and language institutes: examining iranian efl students’ knowledge of listening, reading grammar and vocabulary
هدف از پژوهش حاضر مقایسه زبان آموزان مدارس دوزبانه و موسسات آموزش زبان انگلیسی به منظور تعیین هر گونه تفاوت معنادار در مهارت های درک مطلب، درک شنیداری، دانش دستوری و دانش واژگان است. اطلاعات لازم برای این پژوهش از مجموعه 197 نفر دانش آموز پسر در مدارس دوزبانه و موسسات آموزش زبان جمع آوری شده است. تمامی شرکت کنندگان به مدت چهار الی پنج سال در کلاس های زبان انگلیسی شرکت کرده اند. به منظور جمع آور...
ذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Luminescence
سال: 2021
ISSN: ['1872-7883', '0022-2313']
DOI: https://doi.org/10.1016/j.jlumin.2021.118460