Comparative study of free-volume changes in light-cured (dimeth)acrylate-type dental resin composites affected to artificial aging in dry-air and water-immersed mode
نویسندگان
چکیده
This research is intended to compare degradation processes in light-cured (dimeth)acrylate-type polymer/filler dental composites affected aging dry-air and water-immersed mode. The positron annihilation lifetime (PAL) spectroscopy has been employed study changes atomic-deficient structure these under aging. Under light-curing polymerization initiating crosslinking of monomer chains, fragmentation free-volume holes resin matrix dominates over enhanced fraction trapped positrons, since filler–particles assemblies get be more tightly covered by surrounding polymer causing disappearing interfacial voids at the filler–polymer surface. Therefore, PAL spectra-transforming trend obeys inverse positron-to-Ps trapping conversion. In contrast, restoratives direct Ps-to-positron After aging, observed density sites are ascribed a strong agglomeration Ps-decay sub-system accompanied weaker appearance traps sub-system. water Ps-decaying suppressed due absorbed molecules, this effect being slightly revealed lower polymerization. New interfaces all composites. agglomerated inside artificially aged cause their progressive microcracking.
منابع مشابه
comparative study of pain relieving effect of dry cotton pellet and eugenol cotton pellet in the reduction of pain in emergoney pulpotomy
چکیده ندارد.
15 صفحه اولa comparative study of the relationship between self-, peer-, and teacher-assessments in productive skills
تمایل به ارزیابی جایگزین و تعویض آن با آزمون سنتی مداد و کاغذ در سالهای اخیر افزایش یافته است. اکثر زبان آموزان در کلاس های زبان از نمره نهایی که استاد تعیین میکند ناراضی اند. این تحقیق جهت بررسی ارزیابی در کلاس های زبان انگلیسی به هدف رضایتمندی زبان آموزان از نمره هایشان انجام گرفته است که در آن نمرات ارائه شده توسط سه گروه ارزیاب (ارزیابی خود دانشجو، همسالان واستاد) در مهارت های تولید (تکل...
15 صفحه اولComparative study of the fluorescence intensity of dental composites and human teeth submitted to artificial aging.
The aim of this study was to evaluate quantitatively the fluorescence of resin composites and human teeth, and to determine the stability of fluorescence after aging. Ten specimens were built using a 1 mm thick increment of dentin composite overlapped by a 0.5 mm thick increment of enamel composite. Ten sound human molars were sectioned and silicon carbide-polished to obtain enamel and dentin s...
متن کاملDiametral tensile strength of two dental composites when immersed in ethanol, distilled water and artificial saliva.
OBJECTIVE To examine the effect of distilled water, artificial saliva and ethanol on the tensile strength of direct tooth-coloured restorative material. METHODS The study was conducted at Dr. Ishrat ul Ebad Khan Institute of Oral Health Sciences, Dow University of Health Sciences (DUHS), Karachi, from April 2011 to September 2012. The testing was performed at the Pakistan Council of Scientifi...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Applied Nanoscience
سال: 2021
ISSN: ['2190-5517', '2190-5509']
DOI: https://doi.org/10.1007/s13204-021-01681-2