Combustibility and Thermal Degradation Property of Epoxy Resins with Different Molecular Weight
نویسندگان
چکیده
منابع مشابه
Effect of structure on thermal behaviour of epoxy resins
The paper deals with the curing behaviour of diglycidyl ether of bisphenol-A (DGEBA) using three novel multifunctional aromatic amines having phosphine oxide and amide-acid linkages. The amines were prepared by reacting tris(3-aminophenyl)phosphine oxide (TAP) with 1,2,4,5-benzenetetracarboxylic acid anhydride (P)/4,4-(hexafluoroisopropylidene)diphthalic acid anhydride (F)/3,3,4,4-benzophenonet...
متن کاملInvestigation of the Creep Property of Fast-growing Poplar Wood Modified with Low Molecular Weight Resins
Fast-growing poplar wood was modified with low molecular weight ureaformaldehyde resin (UF) at 41.5% concentration or phenol-formaldehyde (PF) at concentrations of 15, 25, and 40%. The physical and mechanical properties were measured, and creep behavior tests were carried out under ambient indoor conditions. The specimens were subjected to 30 and 50% of their maximum bending load. The density, ...
متن کاملStudy of Hyperbranched Poly(ethyleneimine) Polymers of Different Molecular Weight and Their Interaction with Epoxy Resin
Two different commercial hyperbranched poly(ethyleneimine)s (HBPEI), with molecular weights (MW) of 800 and 25,000 g/mol, and denoted as PEI800 and PEI25000, respectively, as well as the mixtures with a Diglycidyl Ether of Bisphenol-A (DGEBA) epoxy resin, have been studied using thermal analysis techniques (DSC, TGA), dielectric relaxation spectroscopy (DRS), and dynamic mechanical analysis (DM...
متن کاملPreparation and molecular weight determination of soya-beans and benniseed oil-modified alkyd resins
Alkyd resins were prepared into four different sets by varying the percentage concentrationof the glycerol content. Various properties such as the viscosity, Surface drying time, solubilityand color of the alkyd resins were evaluated for the various sets. The alkyd resin with the highestglycerol content was the most viscous, brownish in color and having the highest molecularweight this is due t...
متن کاملSynthesis and Thermal Degradation Studies of Melamine Formaldehyde Resins
Melamine formaldehyde (MF) resins have been synthesized at different reaction temperature and pH values. Different molar ratios of melamine and formaldehyde were used to synthesize the corresponding resins. The prepared resin samples were characterized by using molecular weight determination viscometry and thermogravimetric analysis (TGA). The maximum percentage of solid content (69.7%) was obt...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Society of Materials Science, Japan
سال: 2009
ISSN: 1880-7488,0514-5163
DOI: 10.2472/jsms.58.251