Coloring of anodic oxide coatings on aluminum by the PVD method.
نویسندگان
چکیده
منابع مشابه
Anodic aluminum oxide microchannel plates
A new material for microchannel plates (MCP) is proposed — anodic aluminum oxide. Microchannel plates made of this material may be much cheaper than with conventional lead glass MCP. Also a significantly smaller channel diameter (up to 70 nm) is easily achievable, which means better spatial resolution and the possibility to operate in strong magnetic fields. Methods and means are developed for ...
متن کاملOptimization of the FeCo nanowire fabrication embedded in anodic aluminum oxide template by response surface methodology
Anodic aluminum oxide (AAO) fabricated by two step anodization technique, is used as a template to synthesize FeCo nanowire arrays by AC electrodeposition technique. Response surface methodology (RSM) is applied to design the experiments, fit an empirical model and optimize the conditions to achieve the best magnetic properties. The magnetic properties, pore dimensions, composition and structur...
متن کاملPVD coatings on aluminium substrates
It is well known that aluminium is today the most widely used metallic material besides steel. The mechanical characteristics of aluminium offer an increasing application field, especially where lightweight constructions are required. The demands for improved characteristics such as higher strength and greater durability are achieved by the development of new aluminium alloys. Continuous effort...
متن کاملCorrosion Resistance Improvement of Aluminum by Hydrophobic Anodic Oxide Film
Diminishing surface wettability is an effective method to improve corrosion resistance of aluminum. Various techniques for preparing hydrophobic surface have been reported, most of which use organic coating as the final step. The key point to diminish surface wettability is to form a fine regular surface structure, and the porous type anodic oxide film (PAOF) has nano-pore structure, therefore ...
متن کاملSelf-ordered anodic aluminum oxide formed by H2SO4 hard anodization.
The self-ordering of nanoporous anodic aluminum oxide (AAO) in the course of the hard anodization (HA) of aluminum in sulfuric acid (H2SO4) solutions at anodization voltages ranging from 27 to 80 V was investigated. Direct H2SO4-HA yielded AAOs with hexagonal pore arrays having interpore distances D(int) ranging from 72 to 145 nm. However, the AAOs were mechanically unstable and cracks formed a...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Japan Institute of Light Metals
سال: 1988
ISSN: 0451-5994
DOI: 10.2464/jilm.38.177