Cold-spray coating of an Fe-40 at.% Al alloy with additions of ruthenium
نویسندگان
چکیده
منابع مشابه
Corrosion of Cold Spray Deposited Copper Coating on Steel Substrates
The corrosion behavior of copper cold spray coatings on a carbon steel substrate was compared to that of commercially available wrought copper under the conditions anticipated in a nuclear waste repository. Corrosion potential and linear polarization resistance measurements were conducted over 90 d to 120 d in 3.0 mol/L NaCl under anoxic (1) and oxygenated-toanoxic (2) conditions to simulate th...
متن کاملan investigation of the types of text reduction in subtitling: a case study of the persian film gilaneh with english subtitles
چکیده ندارد.
15 صفحه اولMicrostructural evolution during isothermal annealing of a cold-rolled Al-Mn-Fe-Si alloy with different microchemistry states
In this paper, investigation of the softening behaviour of a supersaturated Al-Mn-Fe-Si alloy during annealing after cold rolling has been carried out. Two different homogenization conditions were considered, of which one gives a condition of a large amount of small pre-existing dispersoids, i.e. providing a significant static Zener drag, while the other gives a condition where both concurrent ...
متن کاملElectrochemical Evaluation of Polyvinyl Butyral Coating Containing Polypyrrole/ZnO Nanocomposite for Corrosion protection of Al Alloy
In this work, polypyrrole/ZnO nanocomposite (PPy/ZnO NC) was produced through synthesis of polypyrrole polymer in the presence of ZnO nanoparticles. The corrosion behavior of polyvinyl butyral coatings without and with different weight percentages of nanocomposite on the surface of 7075 Al alloy was investigated in 3.5% NaCl solution at different immersion times using electrochemical impedance ...
متن کاملKinetics of Austenite Recrystallization during the Annealing of Cold-rolled Fe-Mn-Al-C Steel
In the current study, the recrystallization behavior of 75% cold-rolled Fe-22Mn-10Al-1.4C steel during annealing at 750, 770, 790, 810, and 830°C was studied. X-ray diffraction patterns and optical microscopy were used to characterize microstructures. The Vickers Micro-hardness test was used to characterize recrystallization kinetics during annealing. Johnson-Mehl-Avrami-Kolmogorov (JMAK) model...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Southern African Institute of Mining and Metallurgy
سال: 2016
ISSN: 2411-9717
DOI: 10.17159/2411-9717/2016/v116n10a6