Co-Sintering of Dense Electrophoretically Deposited YSZ Films on Porous NiO-YSZ Substrates for SOFC Applications
نویسندگان
چکیده
منابع مشابه
Fabrication and Characterizations of YSZ Electrolyte Films for SOFC
Yttria stabilized zirconia (YSZ) has been widely used as electrolyte in solid oxide fuel cell (SOFC). The effect of fabrication process on the properties of YSZ electrolyte thick film is discussed in the paper. With YSZ nano-powders of about 20-60nm as raw material, YSZ green adobe was fabricated by tape calendering process. Three-step sintering process was performed firstly holding at 1000°C f...
متن کاملPreparation of NiO-YSZ/YSZ bi-layers for solid oxide fuel cells by electrophoretic deposition
A simple and cost-effective method, starting with electrophoretic deposition (EPD) on a carbon sheet, has been developed for preparation of a iO-YSZ anode and thin, gas-tight YSZ electrolyte layer on it for use in solid oxide fuel cells (SOFCs). The innovative feature of this approach nables the deposition of anode materials as well as the YSZ electrolyte, which were subsequently co-fired in ai...
متن کاملCharacterization of YSZ-YST Composites for SOFC Anodes
Porous composites of Sr0.88Y0.08TiO3-δ (YST) and yttria-stabilized zirconia (YSZ) were formed by tapecasting methods and examined as potential anodes for SOFC. Even after calcination to 1773 K, the YSZ and YST crystallites remain as separate phases, as demonstrated by XRD and SEM with EDX analysis. Furthermore, it was possible to fabricate anode-supported electrolytes by calcination of a bilaye...
متن کاملSOFC Anodes Based on LST–YSZ Composites and on Y0.04Ce0.48ZrM0.48O2
The properties of solid oxide fuel cell (SOFC) anode functional layers prepared by impregnation of 1 wt % Pd and 10 wt % ceria into porous scaffolds of either Y0.04Ce0.48Zr0.48O2 (CZY) or composites of La0.3Sr0.7TiO3 (LST) and yttria-stabilized zirconia (YSZ) were examined to determine whether these scaffold materials would have sufficient electronic and ionic conductivity. Laminated tapes were...
متن کاملMechanical properties of highly textured porous Ni - YSZ and Co - YSZ cermets produced from Directionally Solidified Eutectics
It is well known that several ceramic materials develop an usual; and sometimes unique; combination of properties as a result of mixing different phases with similar expansion coefficients. Sometimes they are elastically stiff, have relatively low thermal expansion coefficients, good thermal and electrical conductivities, and are resistant to chemical attack. As this paper will show, their mech...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: MRS Proceedings
سال: 2004
ISSN: 0272-9172,1946-4274
DOI: 10.1557/proc-835-k3.1