Co-Precipitation, Strength and Electrical Resistivity of Cu–26 wt % Ag–0.1 wt % Fe Alloy
Both a Cu-26 wt % Ag (Fe-free) alloy and Cu-26 wt % Ag-0.1 wt % Fe (Fe-doping) alloy were subjected to different heat treatments. We studied the precipitation kinetics of Ag and Cu, microstructure evolution, magnetization, hardness, strength, and electrical resistivity of the two alloys. Fe addition was incapable of changing the precipitation kinetics of Ag and Cu; however, it decreased the siz...
متن کاملCeramic bonding strength of Au-1.6 wt% Ti alloy.
The aim of this investigation was to evaluate the metal-ceramic bonding of Au-1.6 wt% Ti alloy. Therefore, the coefficient of thermal expansion, modulus of elasticity, ceramic bonding strength, and hardness of Au-1.6 wt% Ti alloy were measured. The metal-ceramic interface was observed by EPMA to investigate its bonding mechanism. The Au-1.6 wt% Ti alloy showed a coefficient of thermal expansion...
متن کاملCyclic Martensitic Transformations Influence on the Diffusion Of Carbon Atoms in Fe-18 wt.%Mn-2 wt.%Si alloy
A significant carbon diffusion mobility acceleration as a result of cyclic γ↔ε martensitic transformations in iron-manganese alloy is determined by one- and two-dimensional structure defects of ε-martensite with face-centered close-packed lattice. Such defects (dislocations, low angle sub-boundaries of dislocations, chaotic stacking faults) were formed during cyclic γ↔ε martensitic transformati...
متن کاملTHE EFFECT OF HEAT TREATMENT ON ABRASIVE WEAR RESISTANCE OF Fe-34Cr-4.5C%WT HARDFACING ALLOY
Abstract: Hardfacing is one of the most useful and economical ways to increase the service life of components subjected to abrasive wear. Iron based hardfacing alloys have long been considered as candidate coatings for wear-resistant applications in industry. In the present work two layer of Fe-34Cr-4.5C%wt hardfacing alloy was deposited on ASTM A36 carbon steel plates by SMAW method. The m...
متن کاملPREPARATION AND SINTERING OF W-20%Wt Cu COMPOSITE POWDERS PRODUCED BY CO-PRECIPITATION METHOD
Abstract: materials can be fabricated by sintering of W-Cu composite powders. In this research W-20%wt Cu composite powderswas synthesized via a co-precipitation method. Precipitate obtained from a mixture of copper nitrate and ammoniumparatungstate (APT) in distilled water contained W-Cu compounds. This precipitate was washed, dried and calcinedat 550 of dried precipitate powder was determined...