Clinical evaluation of ethyl silicate investment for dental use. Castability, surface and accuracy.
نویسندگان
چکیده
منابع مشابه
Surface characteristics and castability of Zr-14Nb alloy dental castings.
The purpose of this study was to evaluate mechanical properties, surface characteristics and castability of Zr-14Nb dental castings. The mean 0.2% proof and ultimate tensile strengths of Zr-14Nb were approximately 68% and 76% those of Ti-6Al-7Nb, respectively, while they were comparable to Co-29Cr-6Mo. Elongation of Zr-14Nb was the highest of all alloys tested. The hardened reaction layer was f...
متن کاملCastability and surface hardness of titanium cast plates obtained from experimental phosphate-bonded silica investment molds.
The effect of 12 different experimental compositions of phosphate-bonded SiO2 investments was examined on cast pure titanium. The mold temperature was 600 degrees C and the casting was conducted with an argon-arc melting and pressure casting machine. Castability was evaluated by the volume of casting porosity, which was calculated from the volume of wax pattern (15 mm x 15 mm x 1.5 mm), the wei...
متن کاملpreparation and characterization of new co-fe and fe-mn nano catalysts using resol phenolic resin and response surface methodology study for fischer-tropsch synthesis
کاتالیزورهای co-fe-resol/sio2و fe-mn-resol/sio2 با استفاده از روش ساده و ارزان قیمت همرسوبی تهیه شدند. از رزین پلیمری resol در فرآیند تهیه کاتالیزور استفاده شد.
the use of appropriate madm model for ranking the vendors of mci equipments using fuzzy approach
abstract nowadays, the science of decision making has been paid to more attention due to the complexity of the problems of suppliers selection. as known, one of the efficient tools in economic and human resources development is the extension of communication networks in developing countries. so, the proper selection of suppliers of tc equipments is of concern very much. in this study, a ...
15 صفحه اولmodification of nanoclay for improving the physico-mechanical properties of dental adhesives
هدف اصلی این مطالعه تهیه یک سامانه نوین چسب عاجی دندانی بر پایه نانورس پیوند شده با پلی متاکریلیک اسید، نانورس پیوند شده با پلی اکریلیک اسید، مخلوط نانوسیلیکا و نانورس پیوند شده با پلی متاکریلیک اسید، مخلوط نانوسیلیکا و نانورس پیوند شده با پلی اکریلیک اسید و نانورس پیوند شده با کیتوسان اصلاح شده با گلایسیدیل متاکریلات است. پیوند پلی متاکریلیک اسید و پلی اکریلیک اسید بر ری سطح نانورس در حضور و ...
ذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Nihon Hotetsu Shika Gakkai Zasshi
سال: 1991
ISSN: 1883-177X,0389-5386
DOI: 10.2186/jjps.35.36